Influence of Ta content in high purity niobium on cavity performance
In a previous paper [1] we have reported about initial tests of single cell 1500 MHz cavities made from high purity niobium with three different Ta contents of 160 ppm , {approx}600 ppm and {approx}1400 ppm. These cavities had been treated by buffered chemical polishing several times and 100 {micro}m, 200 {micro}m and 300 {micro}m of material had been removed from the surfaces. This contribution reports about subsequent tests following post purification heat treatments with Ti and ''in situ'' baking. As a result, all cavities exhibited increased quench fields due to the improved thermal conductivity after the heat treatment. After the ''in situ'' baking at 120 C for {approx} 40 hrs the always present Q-drop at high fields disappeared and further improvements in accelerating gradient could be realized. Gradients as high as E{sub acc} = 35 MV/m were achieved and there were no clear indications that the cavity performance was influenced by the Ta content in the material. A multi-cell cavity from the high Ta content material has been fabricated and initial results are reported.
- Research Organization:
- Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States)
- Sponsoring Organization:
- USDOE; USDOE Office of Energy Research (ER) (US)
- DOE Contract Number:
- AC05-84ER40150
- OSTI ID:
- 840005
- Report Number(s):
- JLAB-ACC-05-340; DOE/ER/40150-3365; TRN: US0501766
- Resource Relation:
- Conference: PAC 2005, Knoxville, TN (US), 05/16/2005--05/20/2005; Other Information: PBD: 1 May 2005
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of Seamless Niobium Cavities for Accelerator Application
PERFORMANCES OF HIGH PURITY NIOBIUM CAVITIES WITH DIFFERENT GRAIN SIZES