Milliwatt generator heat source shelf-life-related pressure-burst capsule evaluations
Three Milliwatt Generator Heat Source (MWGHS) shelf-life-related capsules were pressure-burst tested after thermal aging. Shelf-life capsules PB-08-03 (MC2893) and MPT-11-33 (MC3599) were tested at 1,010 C and capsule PB-07-13 (MC2893) was tested at 1,100 C. Subsequent to pressure-burst testing, each capsule was bubble-leak tested then metallographically examined. Post-mortem evaluation consisted of metallography, microhardness, scanning electron microscopy (SEM), and oxygen and nitrogen analysis. Capsules PB-08-03 and PB-07-13 failed by elevated temperature stress-rupture in the coarse-grained cap to body welds, as has been documented for previous capsules. Pressure-burst testing of capsule MPT-11-33 was terminated prior to failure after 739 hours on test at 1,010 C, however, microscopic examination of the weld indicated that similar failure had began to occur in the interior portion of the capsule to body weld. Evidence was obtained indicating that metallurgical changes occurred during the pressure-burst test performed at 1,100 C. The metallurgical observations of a preferred site for elevated temperature deformation and fracture (the coarse-grained weld region) and structural instability (the property changes during testing at 1,100 C) need to be considered in component lifetime prediction and modeling efforts.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 541946
- Report Number(s):
- SAND-97-2609; ON: DE98000890; BR: DP0401012; TRN: 98:000186
- Resource Relation:
- Other Information: PBD: Oct 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Milliwatt generator heat source. Progress report, July-December 1983
The metallurgical and mechanical properties of ODS alloy MA 956 friction welds