Charpy impact test results of four low activation ferritic alloys irradiated at 370{degrees}C to 15 DPA
- Pacific Northwest National Lab., Richland, WA (United States)
Miniature CVN specimens of four low activation ferritic alloys have been impact tested following irradiation at 370{degrees}C to 15 dpa. Comparison of the results with those of control specimens indicates that degradation in the impact behavior occurs in each of these four alloys. The 9Cr-2W alloy referred to as GA3X and the similar alloy F82H with 7.8Cr-2W appear most promising for further consideration as candidate structural materials in fusion energy system applications. These two alloys exhibit a small DBTT shift to higher temperatures but show increased absorbed energy on the upper shelf.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 414869
- Report Number(s):
- DOE/ER-0313/20; ON: DE97000700; TRN: 97:001388
- Resource Relation:
- Other Information: PBD: Oct 1996; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending June 30, 1996; PB: 358 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Further Charpy impact test results of low activation ferritic alloys, irradiated at 430{degrees}C to 67 dpa
Charpy impact test results for low activation ferritic alloys irradiated to 30 dpa
Charpy impact test results of ferritic alloys irradiated to 10 DPA at 55/degree/C
Technical Report
·
Tue Apr 01 00:00:00 EST 1997
·
OSTI ID:414869
Charpy impact test results for low activation ferritic alloys irradiated to 30 dpa
Technical Report
·
Mon Apr 01 00:00:00 EST 1996
·
OSTI ID:414869
Charpy impact test results of ferritic alloys irradiated to 10 DPA at 55/degree/C
Conference
·
Fri Jul 01 00:00:00 EDT 1988
·
OSTI ID:414869