EXPERIMENTAL GAS COOLED REACTOR-CREEP TEST, AGOT GRAPHITE
Tests were conducted to determine the cumulative and permanent deflection of a beam subjected to two-point loading for (1) ambient temperature- atmospheric environment, and (2) 800 deg F-atmospheric environment, for 8OO psi maximum flexural stresses. Deflection curves are given for five specimens. An analysis of the data indicated that if the core graphite creeps while at EGCR conditions by approximately 1.5 times its creep rate at ambient temperature, the stresses will level off below 1000 psi. Considerable oxidation oc curred for two specimens at 800 deg F. The indicated strain of these specimens may not be representative of AGOT, nuclear grade graphite at 800 deg F in an inert atmosphere. (B.O.G.)
- Research Organization:
- Allis-Chalmers Mfg. Co. Nuclear Power Dept., Washington, D.C.
- NSA Number:
- NSA-15-007781
- OSTI ID:
- 4102161
- Report Number(s):
- TID-11583; RD-0202
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
GAS-COOLED REACTOR PROJECT QUARTERLY PROGRESS REPORT FOR PERIOD ENDING SEPTEMBER 30, 1960
SHEAR TEST OF AGOT GRAPHITE
TENSILE AND CREEP BEHAVIOR OF GRAPHITES AT TEMPERATURES ABOVE 3000 F. Progress Report
Technical Report
·
Fri Nov 11 00:00:00 EST 1960
·
OSTI ID:4102161
SHEAR TEST OF AGOT GRAPHITE
Technical Report
·
Wed Feb 17 00:00:00 EST 1960
·
OSTI ID:4102161
TENSILE AND CREEP BEHAVIOR OF GRAPHITES AT TEMPERATURES ABOVE 3000 F. Progress Report
Technical Report
·
Thu Oct 15 00:00:00 EDT 1959
·
OSTI ID:4102161
+1 more