THE BORON-CARBON SYSTEM. Final Technical Report, May 1, 1960-April 30, 1961
The boron--carbon equilibrium diagram was determined by x-ray, metallographic, and thermal analysis of sintered and arc-cast alloys. A single carbide having a range of solubility from approximately 9 to 20 at.% carbon and melting congruently exists in the system. The terminal solubility of carbon in boron is 0.1-0.2 at.%. The freezing reaction between boron and the carbide is a degenerate peritectic --eutectic reaction at the composition and melting temperature of elemental boron; there is a eutectic reaction at 29 at.% carbon and 2375 deg C. No allotropy of boron was observed. (auth)
- Research Organization:
- Illinois Inst. of Tech., Chicago. Armour Research Foundation
- DOE Contract Number:
- AT(11-1)-578
- NSA Number:
- NSA-15-026534
- OSTI ID:
- 4003641
- Report Number(s):
- ARF-2200-12
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE BORON-CARBON SYSTEM. Quarterly Report No. 3, November 1, 1960-January 31, 1961
THE BORON-CARBON SYSTEM. Quarterly Report No. 2 for August 1, 1960 - October 31, 1960
REGULARITIES IN CREEP AND HOT FATIGUE DATA. PART II
Technical Report
·
Wed Feb 01 00:00:00 EST 1961
·
OSTI ID:4003641
THE BORON-CARBON SYSTEM. Quarterly Report No. 2 for August 1, 1960 - October 31, 1960
Technical Report
·
Tue Nov 01 00:00:00 EST 1960
·
OSTI ID:4003641
REGULARITIES IN CREEP AND HOT FATIGUE DATA. PART II
Technical Report
·
Sat Dec 01 00:00:00 EST 1956
·
OSTI ID:4003641