Metal-insulator transition and doping-induced phase change in Ge2Sb2Se5xTe5-5x
- University of Virginia, Charlottesville, VA (United States). Dept. of Physics
- Department of Emerging Materials Science, DGIST, Daegu (South Korea)
Ge2Sb2Te5 (GST-225), a phase change material (PCM) with vast differences in the electrical and optical characteristics between its amorphous and crystalline phases, is revisited to explore its properties with Se doping. GST crystallizes in a layered hexagonal ground state, while the precursor to the amorphous state is a distorted rock salt like structure with vacancies at the Ge/Sb sites. Upon doping, liquid nitrogen quenched Ge2Sb2Se5xTe5-5x (GSST-225) exhibits a direct hexagonal-to-amorphous phase change above x > 0.8, whereas the rock salt like structure appears as a second phase with a volume fraction that does not change as a function of the doping. The phase change is accompanied by a metal-to-insulator transition (MIT), with a several orders of magnitude increase in the resistivity on approaching the amorphous state. Additionally, a similar MIT is observed even without the phase change in hexagonal crystals with doping levels above x >0.8. On warming amorphous GSST (x = 0.9) above room temperature, a reversal to the hexagonal phase occurs with a re-crystallization onset temperature (Tc) above 300 °C, much higher than the Tc (~170 °C) of amorphous GST and an activation energy of 1.47 eV, which is comparable to good glass formers.
- Research Organization:
- Univ. of Virginia, Charlottesville, VA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- Grant/Contract Number:
- FG02-01ER45927
- OSTI ID:
- 1849393
- Alternate ID(s):
- OSTI ID: 1712506
- Journal Information:
- Applied Physics Letters, Vol. 117, Issue 19; ISSN 0003-6951
- Publisher:
- American Institute of Physics (AIP)Copyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cr-doped Ge{sub 2}Sb{sub 2}Te{sub 5} for ultra-long data retention phase change memory
Fundamental Mechanisms Driving the Amorphous to Crystalline Phase Transformation