Capacitance of coarse-grained carbon electrodes with thickness up to 800 μm

Journal Article · Tue Feb 05 00:00:00 EST 2019 · Electrochimica Acta

DOI:https://doi.org/10.1016/j.electacta.2019.02.004· OSTI ID:1495941

Liu, Liying ^[1]; Wang, Xuehang ^[2]; Izotov, Vladimir ^[1]; Havrykov, Dmytro ^[1]; Koltsov, Illia ^[1]; Han, Wei ^[1]; Zozulya, Yulia ^[3]; Linyucheva, Olga ^[3]; Zahorodna, Veronika ^[4]; Gogotsi, Oleksiy ^[4]; Gogotsi, Yury ^[5]

---

1. Jilin University, Changchun (China)
2. Drexel Univ., Philadelphia, PA (United States)
3. Materials Research Center, Kiev (Ukraine)
4. Materials Research Center, Kiev (Ukraine); National Metallurgical Academy of Ukraine, Dnipro (Ukraine)
5. Jilin University, Changchun (China); Drexel Univ., Philadelphia, PA (United States)

We report that increasing the mass loading of active material in a supercapacitor electrode improves the energy storage capability per electrode area. However, the increase of mass loading is accompanied by the increased electrode thickness, which often causes drops in specific capacitance and counteracts the potential increase in areal capacitance once the electrode thickness exceeds 100 μm. In our previous work, we showed high specific capacitance retention of coarse-grained carbide derived carbon (CDC) with electrode thicknesses up to 1000 μm in organic electrolytes. In this work, we report that this behavior can be extended to coarse-grained activated carbon (AC). AC is the most common commercial supercapacitor electrode material with a much broader pore size distribution and lower electric conductivity compared to CDC. The areal capacitance of the AC electrode is enhanced from 2.3 F/cm² to 7.4 F/cm² at 5 mV/s, as the electrode thickness increases from 200 to 800 μm. With the increased mass loading of the active electrode material, the mass and volume occupied by current collectors and separators are reduced in the electrode stack, which leads to an increase of the gravimetric and volumetric energy density of the device. Finally, by reporting on this advantageous behavior in thick electrodes using coarse-grained carbons, we hope to garner interest toward an unexplored method for improving the performance of porous carbon-based supercapacitors, without increasing the cost or changing the current used supercapacitor manufacturing process.

• Research Organization: Energy Frontier Research Centers (EFRC) (United States). Fluid Interface Reactions, Structures and Transport Center (FIRST); Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
• Sponsoring Organization: USDOE Office of Science (SC), Basic Energy Sciences (BES)
• Grant/Contract Number: AC05-00OR22725
• OSTI ID: 1495941
• Journal Information: Electrochimica Acta, Vol. 302, Issue C; ISSN 0013-4686
• Publisher: Elsevier
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
Supercapacitor
Coarse-grained carbon
Thick electrode
High areal capacitance
Activated carbon
And carbide derived carbon