Nonequilibrium Synthesis of Highly Porous Single-Crystalline Oxide Nanostructures
Journal Article
·
· Advanced Materials Interfaces
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
A novel synthesis route to the formation of vertically aligned single–crystalline oxide nanostructures is found by precisely controlling the nonequilibrium pulsed laser deposition process. Here, the columnar nanostructures with deep crevices offering a large surface area are generated owing to the diffusion limited geometric shadowing effect.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1436958
- Alternate ID(s):
- OSTI ID: 1401742
- Journal Information:
- Advanced Materials Interfaces, Vol. 4, Issue 3; ISSN 2196-7350
- Publisher:
- Wiley-VCHCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Cited by: 11 works
Citation information provided by
Web of Science
Web of Science
Colossal oxygen vacancy formation at a fluorite-bixbyite interface
|
journal | March 2020 |
Similar Records
Preparation of highly ordered growth of single-crystalline Gd{sub 2}O{sub 2}S:Eu{sup 3+} nanostructures
Vertically Aligned Single-Crystalline CoFe2O4 Nanobrush Architectures with High Magnetization and Tailored Magnetic Anisotropy
Self-Assembled, Nanostructured, Tunable Metamaterials via Spinodal Decomposition
Journal Article
·
Tue Feb 15 00:00:00 EST 2011
· Materials Research Bulletin
·
OSTI ID:1436958
Vertically Aligned Single-Crystalline CoFe2O4 Nanobrush Architectures with High Magnetization and Tailored Magnetic Anisotropy
Journal Article
·
Thu Mar 05 00:00:00 EST 2020
· Nanomaterials
·
OSTI ID:1436958
+9 more
Self-Assembled, Nanostructured, Tunable Metamaterials via Spinodal Decomposition
Journal Article
·
Wed Nov 09 00:00:00 EST 2016
· ACS Nano
·
OSTI ID:1436958
+9 more