Mixed-mode I/III fracture toughness of a ferritic/martensitic stainless steel
- Associated Western Univ., Richland, WA (United States)
- Pacific Northwest Lab., Richland, WA (United States)
- Washington State Univ., Pullman, WA (United States)
The critical J-integrals of mode I (J{sub IC}), mixed-mode I/III (J{sub MC}), and mode III (J{sub IIIC}) were examined for a ferritic stainless steel (F-82H) at ambient temperature. A determination of J{sub MC} was made using modified compact-tension specimens. Different ratios of tension/shear stress were achieved by varying the principal axis of the crack plane between 0 and 55 degrees from the load line. Results showed that J{sub MC} and tearing modulus (T{sub M}) values varied with the crack angles and were lower than their mode I and mode III counterparts. Both the minimum J{sub MC} and T{sub M} values occurred at a crack angle between 40 and 50 degrees, where the load ratio of {sigma}{sub i}/{sigma}{sub iii} was 1.2 to 0.84. The J{sub min} was 240 Kj/M{sup 2}, and ratios of J{sub IC}/J{sub min} and J{sub IIIC}/J{sub min} were 2.1 and 1.9, respectively. The morphology of fracture surfaces was consistent with the change of J{sub MC} and T{sub M} values. While the upper shelf-fracture toughness of F-82H depends on loading mode, the J{sub min} remains very high. Other important considerations include the effect of mixed-mode loading on the DBT temperature, and effects of hydrogen and irradiation on J{sub min}.
- Research Organization:
- Pacific Northwest Lab., Richland, WA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 10162586
- Report Number(s):
- PNL-SA-22493; CONF-931009-27; ON: DE94014492
- Resource Relation:
- Conference: Fall meeting of the Minerals, Metals and Materials Society: physical metallurgy and materials,Pittsburgh, PA (United States),17-21 Oct 1993; Other Information: PBD: Oct 1993
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of loading mode on the fracture toughness of a ferritic/martensitic stainless steel
Effect of hydrogen on the fracture toughness of a ferritic/martensitic stainless steel