Magneto-optical study of Ba(Fe{sub 1-x}M{sub x}{sub 2}As{sub2} (M = Co and Ni) single crystals irradiated with heavy ions.
Optimally doped single crystals of Ba(Fe{sub 1-x}M{sub x}){sub 2}As{sub 2} (M=Co, Ni) were irradiated with 1.4 GeV {sup 208}Pb{sup 56+} ions at fluences corresponding to matching fields of B{phi} = 0.1, 0.5, 1, and 2 T. Magneto-optical imaging has been used to map the distribution of the magnetic induction in the irradiated samples. The imaging is complemented by the magnetization measurements. The results show a substantial enhancement of the apparent critical current densities as revealed by the much larger Bean penetration fields and an increase in the hysteretic magnetization. However, the effect depends on the compound, temperature, and applied magnetic field. In Ba(Fe{sub 0.926}Co{sub 0.074}){sub 2}As{sub 2} crystals, at 15 K and low fields, the enhancement appears to scale with the irradiation dose at a rate of about 0.27 MA {center_dot} cm{sup -2} T{sup -1}, whereas in Ba(Fe{sub 0.954}Ni{sub 0.046}){sub 2}As{sub 2} crystals, higher irradiation doses are less effective. Our results suggest that moderate irradiation with heavy ions is an effective way to homogeneously enhance the current-currying capabilities of pnictide superconductors.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 993401
- Report Number(s):
- ANL/MSD/JA-68503; TRN: US1008013
- Journal Information:
- Phys. Rev. B, Vol. 81, Issue Mar. 9, 2010
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Studies of anisotropy of iron based superconductors
Growth of nematic susceptibility in the field-induced normal state of an iron-based superconductor revealed by elastoresistivity measurements in a 65 T pulsed magnet