Synthesis, magnetic and dielectric characterization of nanocrystalline solid solutions of In{sub 2−x}Ni{sub x}O{sub 3} (x = 0.05, 0.10 and 0.15)

Journal Article · Sun Sep 01 00:00:00 EDT 2013 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2013.04.051· OSTI ID:22341749

Ahmad, Tokeer ^[1]; Khatoon, Sarvari ^[1]; Coolahan, Kelsey ^[2]

---

1. Nanochemistry Laboratory, Department of Chemistry, Jamia Millia Islamia, New Delhi 110025 (India)
2. Department of Physics and Astronomy, Rowan University, 201 Mullica Hill Road, Glassboro, NJ 08028 (United States)

Graphical abstract: Monophasic and crystalline In{sub 2−x}Ni{sub x}O{sub 3} nanoparticles of size 8–15 nm have been synthesized solvothermally and showed red shift in energy band gap which decreases on increasing Ni{sup 2+} concentration in In{sub 2}O{sub 3} host lattice. - Highlights: • Monophasic Ni-doped In{sub 2}O{sub 3} nanoparticles by solvothermal method for first time. • Plausible reaction mechanism using thermogravimetric analysis. • High surface area with small particle size obtained. • Solid solutions exhibit paramagnetism with very weak antiferromagnetic interactions. - Abstract: In{sub 2−x}Ni{sub x}O{sub 3} (x = 0.05, 0.10 and 0.15) nanoparticles were successfully synthesized by solvothermal method by the thermal decomposition of oxalate precursor at 450 °C for the first time. X-ray diffraction studies showed the formation of highly crystalline and monophasic cubic structure of In{sub 2}O{sub 3} which is attributed to the formation of solid solution. These nanoparticles show good optical transmittance in the visible region. Optical measurements showed an energy band gap which decreases with increasing Ni concentration. The grain size decreases from 15 nm to 8 nm and surface area increases from 90 to 254 m{sup 2} g{sup −1} on increasing the Ni concentration. High dielectric constant and dielectric loss has been obtained which indicates the conducting nature of these solid solutions. Magnetic measurements showed that the samples are strong paramagnetic in nature with very weak antiferromagnetic interactions. No evidence of ferromagnetism is observed for these solid solutions at room temperature.

• OSTI ID: 22341749
• Journal Information: Materials Research Bulletin, Vol. 48, Issue 9; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ANTIFERROMAGNETISM
CRYSTALS
DIELECTRIC MATERIALS
DOPED MATERIALS
FERROMAGNETISM
GRAIN SIZE
INDIUM OXIDES
MAGNETIC PROPERTIES
NANOPARTICLES
NANOSTRUCTURES
OPTICAL PROPERTIES
PARAMAGNETISM
PARTICLE SIZE
PYROLYSIS
REACTION KINETICS
SOLID SOLUTIONS
SYNTHESIS
THERMAL GRAVIMETRIC ANALYSIS
X-RAY DIFFRACTION