Amorphous phase formation in Fe-6.0wt%Si alloy by mechanical alloying
Journal Article
·
· Scripta Materialia
Mechanical alloying, MA, is a high-energy ball milling technique, in which elemental blends are milled to achieve alloying at atomic level. This communication describes the results of an investigation on the phase transformation of a mixture of Fe and Si powders with 6wt%Si during MA processing. Besides the verification of the effect of milling time on the structure and on the compositional homogeneity, this study was undertaken in order to confirm, by using TEM technique, the possibility of amorphous phase formation for Si content lower than 17.7wt%.
- Research Organization:
- Federal Univ. of Sao Carlos (BR)
- OSTI ID:
- 20023079
- Journal Information:
- Scripta Materialia, Vol. 42, Issue 2; Other Information: PBD: 31 Dec 1999; ISSN 1359-6462
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural and nuclear magnetic resonance studies of solid-state amorphization in Al-Ti-Si composites prepared by mechanical alloying
Crystalline-to-amorphous phase transformation in mechanically alloyed Fe{sub 50}W{sub 50} powders
Phase transformation during mechano-synthesis of nanocrystalline/amorphous Fe–32Mn–6Si alloys
Journal Article
·
Mon Aug 16 00:00:00 EDT 2004
· Acta Materialia
·
OSTI ID:20023079
+2 more
Crystalline-to-amorphous phase transformation in mechanically alloyed Fe{sub 50}W{sub 50} powders
Journal Article
·
Sat Mar 01 00:00:00 EST 1997
· Acta Materialia
·
OSTI ID:20023079
Phase transformation during mechano-synthesis of nanocrystalline/amorphous Fe–32Mn–6Si alloys
Journal Article
·
Tue Oct 15 00:00:00 EDT 2013
· Materials Characterization
·
OSTI ID:20023079
+2 more