Superconducting transition width (Δ T c ) characteristics of 25 mol% Zr-added (Gd, Y)Ba 2 Cu 3 O 7− δ superconductor tapes with high in-field critical current density at 30 K
Journal Article
·
· Superconductor Science and Technology
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- Grant/Contract Number:
- AR0000196
- OSTI ID:
- 1332772
- Journal Information:
- Superconductor Science and Technology, Journal Name: Superconductor Science and Technology Vol. 30 Journal Issue: 1; ISSN 0953-2048
- Publisher:
- IOP PublishingCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Cited by: 16 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Requirements to achieve high in-field critical current density at 30 K in heavily-doped (Gd,Y)Ba
2
Cu
3
O
x
superconductor tapes
Strongly enhanced vortex pinning from 4 to 77 K in magnetic fields up to 31 T in 15 mol.% Zr-added (Gd, Y)-Ba-Cu-O superconducting tapes
Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K
Journal Article
·
Mon Aug 24 00:00:00 EDT 2015
· Superconductor Science and Technology
·
OSTI ID:1332772
+2 more
Strongly enhanced vortex pinning from 4 to 77 K in magnetic fields up to 31 T in 15 mol.% Zr-added (Gd, Y)-Ba-Cu-O superconducting tapes
Journal Article
·
Tue Apr 01 00:00:00 EDT 2014
· APL Materials
·
OSTI ID:1332772
+6 more
Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K
Journal Article
·
Tue Mar 11 00:00:00 EDT 2014
· Superconductor Science and Technology
·
OSTI ID:1332772
+5 more