Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K

Journal Article · Tue Mar 11 04:00:00 EDT 2014 · Superconductor Science and Technology

DOI:https://doi.org/10.1088/0953-2048/27/5/055010· OSTI ID:1211370

Selvamanickam, V; Xu, A; Liu, Y; Khatri, ND; Lei, C; Chen, Y; Galstyan, E; Majkic, G

Critical current (I-c) values of 1384 Lambda/12 mm, corresponding to a critical current density of 12.47 MA cm(-2) and a pinning force of 374 GN m(-3), have been achieved at 30 K, 3 T in the orientation of field parallel to the c axis (B parallel to c) in (Gd, Y)BaCuO tapes with 15 mol% Zr addition made by metal organic chemical vapor deposition (MOCVD). These tapes show pinning force levels as high as 453 GN m(-3) at 30 K. An analysis of the properties of 24-28 (Gd, Y)BaCuO tapes with 15 mol% Zr addition showed a lack of correlation between their critical currents at 30 K, 3 T (B parallel to c) and I-c values both at 77 K, zero field and at 77 K, 1 T (B parallel to c). However, a strong correlation was found between the critical currents at 30 K, 3 T and at 77 K, 3 T (B parallel to c). It has also been discovered that the minimum critical current (I-c, (min)) value at 77 K, 3 T has no influence on the I-c,I- (min) value at 30 K, 3 T, and it in turn depends on the ratio of the I-c values in the orientations of field parallel and perpendicular to the c axis at 77 K, 3 T.

• Sponsoring Organization: USDOE Advanced Research Projects Agency - Energy (ARPA-E)
• DOE Contract Number: AR0000196
• OSTI ID: 1211370
• Journal Information: Superconductor Science and Technology, Journal Name: Superconductor Science and Technology Journal Issue: 5 Vol. 27; ISSN 0953-2048
• Country of Publication: United States
• Language: English