High Temperature Measurements Of Martensitic transformations Using Digital Holography
Journal Article
·
· Journal of Applied Optics (Yingyong Guangxue)
- Northern Arizona University
- ORNL
During thermal cycling of nickel-aluminum-platinum (NiAlPt) and single crystal Fe-15Cr-15Ni alloys, the structural changes associated with the martensite to austenite phase transformation were measured using dual-wavelength digital holography. Real-time in-situ measurements reveal the formation of striations within the NiPtAl alloy at 70 C and the FeCrNi alloy at 520 C. The results demonstrate that digital holography is an effective technique for acquiring non-contact, high precision information of the surface evolution of alloys at high temperatures.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Laboratory Directed Research and Development (LDRD) Program
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1086641
- Journal Information:
- Journal of Applied Optics (Yingyong Guangxue), Vol. 52, Issue 19; ISSN 0003--6935
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of the Martensitic Transformation in NiPtAl Alloy Using Digital Holographic Imaging
Microstructural examination of 12% Cr martensitic stainless steel after irradiation at elevated temperatures in FFTF (Fast Flux Test Facility)
Alumina-Forming Austenitic Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates
Journal Article
·
Mon Aug 13 00:00:00 EDT 2018
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:1086641
+2 more
Microstructural examination of 12% Cr martensitic stainless steel after irradiation at elevated temperatures in FFTF (Fast Flux Test Facility)
Conference
·
Sun Jun 01 00:00:00 EDT 1986
·
OSTI ID:1086641
Alumina-Forming Austenitic Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates
Journal Article
·
Mon Jan 01 00:00:00 EST 2007
· Metallurgical and Materials Transactions A
·
OSTI ID:1086641
+4 more