Microstructural examination of 12% Cr martensitic stainless steel after irradiation at elevated temperatures in FFTF (Fast Flux Test Facility)
A remelted 12% Cr martensitic stainless steel (HT-9) has been examined by transmission electron microscopy before and after irradiation in the Materials Open Test Assembly (MOTA) of the Fast Flux Test Facility (FFTF). The irradiation temperatures were 365,420, 520, and 600/degree/C with the fluences as high as 7.3 /times/ 10/sup 22/ n/cm/sup 2/ (E > 0.1 MeV) or 34 dpa. The extracted precipitates from each specimen were identified using x-ray microanalysis and selected area diffraction. The precipitates in the unirradiated condition were primarily M/sub 23/C/sub 6/ carbides, which formed at martensite lath and prior austenite grain boundaries. During irradiation at elevated temperatures, small amounts of other phases formed, which were tentatively identified as the chromium-rich /alpha//prime/, the nickel-silicon rich G-phase, and the intermetallic Chi phase. Irradiation-induced voids were observed only in specimens irradiated at 420/degree/C to a dose of 34 dpa; no voids were found for specimens irradiated at 365, 520, and 600/degree/C (/approximately/11, /approximately/34, and /approximately/34 dpa). These results are not in agreement with previous experiments in that voids have not been reported in this alloy at relatively high fluence level (/approximately/67 dpa) following irradiation in another fast-spectrum reactor (EBR.II). This is, however, the first observation following FFTF irradiation. The present results indicate that cavities can form in HT-9 at modest fluence levels even without significant generation of helium. Hence, the cavity formation in this class of ferritic alloys is not simply caused by helium generation but rather more complex mechanisms. 12 refs., 2 figs., 3 tabs.
- Research Organization:
- Hanford Engineering Development Lab., Richland, WA (USA)
- DOE Contract Number:
- AC06-76FF02170
- OSTI ID:
- 5979459
- Report Number(s):
- HEDL-SA-3564; CONF-860605-47; ON: DE89014954
- Country of Publication:
- United States
- Language:
- English
Similar Records
An investigation of microstructures and yield strengths in irradiated austenitic stainless steels using small specimen techniques
Effects of helium pre-implantation on the microstructure and mechanical properties of irradiated 316 stainless steel
Related Subjects
360106* -- Metals & Alloys-- Radiation Effects
ALLOYS
CARBON ADDITIONS
CHROMIUM
CRYSTAL STRUCTURE
ELECTRON MICROSCOPY
ELEMENTS
FERRITE
IRON ALLOYS
IRRADIATION
MARTENSITE
METALS
MICROSCOPY
MICROSTRUCTURE
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
TRANSITION ELEMENTS
TRANSMISSION ELECTRON MICROSCOPY
VOIDS