Effects of helium pre-implantation on the microstructure and mechanical properties of irradiated 316 stainless steel
- Univ. of California, Santa Barbara, CA (United States). Dept. of Chemical and Nuclear Engineering
- Oak Ridge National Lab., TN (United States)
- Pacific Northwest Lab., Richland, WA (United States)
Transmission electron microscopy (TEM) specimens of a First Core heat of 316 stainless steel, in both the solution annealed and 20% cold worked condition, were irradiated to 46 dpa at 420 C, to 49 dpa at 520 C, and to 34 dpa at 600 C in FFTF/MOTA. Prior to irradiation, about half of the specimens were pre-implanted with approximately 100 appm of helium, and of these, several of the solution annealed and pre-implanted specimens were aged at 800 C for 2 hr. Post-irradiation density measurements showed little difference in density between the unimplanted alloys and their helium implanted counterparts. Microstructural observations on specimens irradiated at 420 C and 520 C showed relatively minor differences in defect distributions between the unimplanted and the helium implanted materials; in all cases the defect sizes and number densities were consistent with data in the literature. Where possible, irradiation hardening of the alloys was experimentally evaluated by microhardness and shear punch; experimentally obtained values were compared to values calculated using a computer model based on barrier hardening and the microstructural data. All methods indicated relatively small effects of helium implantation, and both measured and calculated values were in agreement with the range of values reported in the literature.
- Research Organization:
- Pacific Northwest Lab., Richland, WA (United States); California Univ., Santa Barbara, CA (United States). Dept. of Physics; Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC06-76RL01830; FG03-87ER52143; AC05-84OR21400
- OSTI ID:
- 10119299
- Report Number(s):
- PNL-SA--25670; CONF-941144--60; ON: DE95007162; AT150203A
- Country of Publication:
- United States
- Language:
- English
Similar Records
Proton Irradiation Emulation of PWR Neutron Damage Microstructures in Solution Annealed 304 and Cold-Worked 316 Stainless Steels
Effect of neutron irradiation on the tensile properties and microstructure of several vanadium alloys