Tribological synthesis method for producing low-friction surface film coating

Title: Tribological synthesis method for producing low-friction surface film coating

Full Record
Other Related Research

Abstract

An article of method of manufacture of a low friction tribological film on a substrate. The article includes a substrate of a steel or ceramic which has been tribologically processed with a lubricant containing selected additives and the additives, temperature, load and time of processing can be selectively controlled to bias formation of a film on the substrate where the film is an amorphous structure exhibiting highly advantageous low friction properties.

Inventors:: Ajayi, Oyelayo O.; Lorenzo-Martin, Maria De La; Fenske, George R.

Issue Date:: 2016-10-25

Research Org.:: Argonne National Lab. (ANL), Argonne, IL (United States)

Sponsoring Org.:: USDOE

OSTI Identifier:: 1330342

Patent Number(s):: 9476007

Application Number:: 14/038,121

Assignee:: UChicago Argonne, LLC (Chicago, IL)

Patent Classifications (CPCs):: C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10M - LUBRICATING COMPOSITIONS

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10N - INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS

Show more

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10M - LUBRICATING COMPOSITIONS
C10M2201/0403 - used as base material

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10N - INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
C10N2010/12 - Group 6

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10M - LUBRICATING COMPOSITIONS
C10M2227/066 - derived from Mo or W
C10M2205/0285 - used as base material

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10N - INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
C10N2030/06 - Oiliness

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10M - LUBRICATING COMPOSITIONS
C10M2203/003 - used as base material

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10N - INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
C10N2010/02 - Group 1
C10N2080/00 - Special pretreatment of the material to be lubricated, e.g. phosphatising or chromatising of a metal

C - CHEMISTRY C10 - PETROLEUM, GAS OR COKE INDUSTRIES C10M - LUBRICATING COMPOSITIONS
C10M177/00 - Special methods of preparation of lubricating compositions

Show less

DOE Contract Number:: W-31-109-ENG-38

Resource Type:: Patent

Resource Relation:: Patent File Date: 2013 Sep 26

Country of Publication:: United States

Language:: English

Subject:: 36 MATERIALS SCIENCE

Citation Formats


                    Ajayi, Oyelayo O., Lorenzo-Martin, Maria De La, and Fenske, George R. Tribological synthesis method for producing low-friction surface film coating.  United States: N. p., 2016. 
        Web.

Copy to clipboard


                    Ajayi, Oyelayo O., Lorenzo-Martin, Maria De La, & Fenske, George R. Tribological synthesis method for producing low-friction surface film coating.  United States.

Copy to clipboard


                    Ajayi, Oyelayo O., Lorenzo-Martin, Maria De La, and Fenske, George R. Tue .  
        "Tribological synthesis method for producing low-friction surface film coating".  United States.  https://www.osti.gov/servlets/purl/1330342.

Copy to clipboard


                    
@article{osti_1330342,

  title        = {Tribological synthesis method for producing low-friction surface film coating},

  author       = {Ajayi, Oyelayo O. and Lorenzo-Martin, Maria De La and Fenske, George R.},

  abstractNote = {An article of method of manufacture of a low friction tribological film on a substrate. The article includes a substrate of a steel or ceramic which has been tribologically processed with a lubricant containing selected additives and the additives, temperature, load and time of processing can be selectively controlled to bias formation of a film on the substrate where the film is an amorphous structure exhibiting highly advantageous low friction properties.},

  doi          = {},

  journal      = {},
number       = ,

  volume       = ,

  place        = {United States},

  year         = {2016},

  month        = {10}

}

Copy to clipboard

Patent:

View Patent

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE Patents and OSTI.GOV collections:

Ultra-hard low friction coating based on A1MgB.sub.14 for reduced wear of MEMS and other tribological components and system

Patent Cook, Bruce Allan; Tian, Yun; Harringa, Joel Lee; ...

Performance and reliability of microelectromechanical system (MEMS) components enhanced dramatically through the incorporation of protective thin film coatings. Current-generation MEMS devices prepared by the LIGA technique employ transition metals such as Ni, Cu, Fe, or alloys thereof, and hence lack stability in oxidizing, corrosive, and/or high temperature environments. Fabrication of a superhard, self-lubricating coating based on a ternary boride compound AlMgB.sub.14 is described in this letter as a potential breakthrough in protective coating technology for LIGA microdevices. Nanoindentation tests show that hardness of AlMgB.sub.14 films prepared by pulsed laser deposition ranges from 45 GPa to 51 GPa, when deposited atmore »« less
Full Text Available
Method of produce ultra-low friction carbon films

Patent Erdemir, Ali [Naperville, IL]; Fenske, George R [Downers Grove, IL]; Eryilmaz, Osman Levent [Istanbul, TK]; ...

A method and article of manufacture of amorphous diamond-like carbon. The method involves providing a substrate in a chamber, providing a mixture of a carbon containing gas and hydrogen gas with the mixture adjusted such that the atomic molar ratio of carbon to hydrogen is less than 0.3, including all carbon atoms and all hydrogen atoms in the mixture. A plasma is formed of the mixture and the amorphous diamond-like carbon film is deposited on the substrate. To achieve optimum bonding an intervening bonding layer, such as Si or SiO.sub.2, can be formed from SiH.sub.4 with or without oxidation ofmore » the layer formed.« less
Full Text Available
High temperature low friction surface coating

Patent Bhushan, Bharat [Watervliet, NY]

A high temperature, low friction, flexible coating for metal surfaces which are subject to rubbing contact includes a mixture of three parts graphite and one part cadmium oxide, ball milled in water for four hours, then mixed with thirty percent by weight of sodium silicate in water solution and a few drops of wetting agent. The mixture is sprayed 12-15 microns thick onto an electro-etched metal surface and air dried for thirty minutes, then baked for two hours at 65.degree. C. to remove the water and wetting agent, and baked for an additional eight hours at about 150.degree. C. tomore »« less
Full Text Available
Hard and low friction nitride coatings and methods for forming the same

Patent Erdemir, Ali [Naperville, IL]; Urgen, Mustafa [Istanbul, TR]; Cakir, Ali Fuat [Istanbul, TR]; ...

An improved coating material possessing super-hard and low friction properties and a method for forming the same. The improved coating material includes the use of a noble metal or soft metal homogeneously distributed within a hard nitride material. The addition of small amounts of such metals into nitrides such as molybdenum nitride, titanium nitride, and chromium nitride results in as much as increasing of the hardness of the material as well as decreasing the friction coefficient and increasing the oxidation resistance.
Full Text Available
Composite coating for low friction and wear applications and method thereof

Patent Besmann, Theodore M [Oak Ridge, TN]; Blau, Peter J [Oak Ridge, TN]; Lee, Woo Y [Knoxville, TN]; ...

An article having a multiphase composite lubricant coating of a hard refractory matrix phase of titanium nitride dispersed with particles of a solid lubricating phase of molybdenum disulfide is prepared by heating the article to temperatures between 350.degree. and 850.degree. C. in a reaction vessel at a reduced pressure and passing a gaseous mixture of Ti((CH.sub.3).sub.2 N).sub.4, MoF.sub.6, H.sub.2 S and NH.sub.3 over the heated article forming a multiphase composite lubricant coating on the article.
Full Text Available

Similar Records