Formation and Stability of Shear-Induced Shish-Kebab Structure in Highly Entangled Melts of UHMWPE/HDPE Blends
The formation and stability of a shear-induced shish-kebab structure was investigated by in situ rheo-SAXS (small-angle X-ray scattering) and -WAXD (wide-angle X-ray diffraction) measurements of highly entangled polyethylene melts based on two polymer blends, containing small fractions (2 and 5 wt %) of ultra-high molecular weight polyethylene (UHMWPE) and high-density polyethylene (HDPE). Immediately after shear, the combined SAXS and WAXD results at 142 C confirmed the sole formation of shish without kebabs, indicating the interplay between the topological deformation of highly entangled UHMWPE chains and the extended-chain crystallization of stretched segments without the participation of coiled segments. The presence of HDPE chains influenced the entanglement of UHMWPE but they were not involved in the shish-kebab formation at the initial stage of crystallization. The final shish lengths in both blends were nearly identical at the same strain (e = 500), even though the UHMWPE concentration was different. When the temperature was cooled to 134 C, both sheared blends exhibited the kebab formation, following the diffusion-controlled growth process. Although the total kebab nucleation was higher in the 5/95 wt % UHMWPE/HDPE blend, the kebab density per shish was higher in the 2/98 wt % UHMWPE/HDPE blend. The thermal stability of the shish-kebab structure was also investigated by constrained melting. Both blends exhibited identical melting behavior of kebabs but different melting behavior of shish that is governed by the entanglement restraints of the stretched-chain network.
- Research Organization:
- Brookhaven National Laboratory (BNL) National Synchrotron Light Source
- Sponsoring Organization:
- Doe - Office Of Science
- DOE Contract Number:
- AC02-98CH10886
- OSTI ID:
- 959891
- Report Number(s):
- BNL--82877-2009-JA
- Journal Information:
- Macromolecules, Journal Name: Macromolecules Journal Issue: 13 Vol. 41
- Country of Publication:
- United States
- Language:
- English
Similar Records
Probing the Flow-Induced Shish-Kebab Structure in Entangled Polyethylene Melts by Synchrotron X-ray Scattering
Thermal Stability of Shish-Induced Shish-Kebab Precursor Structure from High Molecular Weight Polyethylene Chains
Probing Nucleation and Growth Behavior of Twisted Kebabs from Shish Scaffold in Sheared Polyethylene Melts by in situ X-ray Studies
Journal Article
·
Sun Dec 31 23:00:00 EST 2006
· Journal of Applied Crystallography
·
OSTI ID:930374
Thermal Stability of Shish-Induced Shish-Kebab Precursor Structure from High Molecular Weight Polyethylene Chains
Journal Article
·
Sat Dec 31 23:00:00 EST 2005
· Macromolecules
·
OSTI ID:914341
Probing Nucleation and Growth Behavior of Twisted Kebabs from Shish Scaffold in Sheared Polyethylene Melts by in situ X-ray Studies
Journal Article
·
Sun Dec 31 23:00:00 EST 2006
· Polymer
·
OSTI ID:929977