Alloying Effects on Creep and Oxidation Resistance of Austenitic Stainless Steel Alloys Employing Intermetallic Precipitates
- ORNL
- Tokyo Institute of Technology
Microstructure evolution during creep testing at 750 C and 100 MPa of Fe-20Cr-30Ni-2Nb (at.%) alloys with and without 0.4 Si, 0.2 Zr or 5.0 Al additions has been studied, in order to explore the viability of Fe-rich austenitic stainless alloys strengthened by intermetallic phases. Fine Fe{sub 2}Nb Laves phase dispersions with the size of less than 1 {micro}m within the {gamma}-Fe matrix were obtained in the base and Si-modified alloys after aging at 800 C. The addition of Si helped to refine and stabilize the size of particles, resulting in finer and denser Fe{sub 2}Nb dispersion than that in the base alloy. The alloys with only solution heat-treatment exhibited superior creep resistance to the aged ones, which is due to dynamic precipitation of the Fe{sub 2}Nb Laves phase during creep testing with a size of 300-400 nm, resulting in more effective pinning of dislocations. The base alloy also showed the meta-stable {gamma}*-Ni{sub 3}Nb phase with a size of 50 nm during the transient state of the creep testing. The Zr-modified alloy achieved significant improvement of creep properties. This is hypothesized to be due to the stabilization of {delta}-Ni{sub 3}Nb phase relative to Fe{sub 2}Nb, resulting in the formation of multiple fine dispersions of stable intermetallic compounds of {delta} and Fe{sub 2}Nb within the {gamma}-Fe matrix. A small amount of a (Ni, Zr and Nb)-enriched unidentified phase was also observed. The addition of Al significantly improved the oxidation resistance because of the formation of protective alumina scales on the surface. The alloy also showed superior creep resistance to that of the base alloy due to the formation of a dense dispersion of spherical Ni{sub 3}Al, typically 30 nm in diameter. Collectively, these findings provide the alloy design basis for creep and oxidation-resistant austenitic stainless steel alloys via intermetallic precipitates.
- Research Organization:
- Oak Ridge National Laboratory (ORNL); Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- FE USDOE - Office of Fossil Energy (FE); SC USDOE - Office of Science (SC)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 936281
- Journal Information:
- Intermetallics, Journal Name: Intermetallics Journal Issue: 3 Vol. 16; ISSN 0966-9795; ISSN IERME5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Alumina-Forming Austenitic Stainless Steels Strengthened by Laves Phase and MC Carbide Precipitates
Overview of strategies for high-temperature creep and oxidation resistance of alumina-forming austenitic stainless steels