Novel Neo-Pentoxide Precursors for MOCVD Thin Films of TiO(2) and ZrO(2).[1]
- Sandia National Laboratories
Two novel Group IV precursors, titanium (IV) neo-pentoxide, [Ti({mu}-ONep)(ONep){sub 3}]{sub 2} (l), and zirconium (IV) neo-pentoxide, [Zr({mu}-ONep)(ONep){sub 3}]{sub 2} (2), were reported to possess relatively high volatility at low temperatures. These compounds were therefore investigated as MOCVD precursors using a lamp-heated cold-wall CVD reactor and direct sublimation without carrier gas. The ONep derivatives proved to be competitive precursors for the production of thin films of the appropriate MO{sub 2} (M = Ti or Zr) materials in comparison to other metallo-organic precursors. Compound 1 was found to sublime at 120 C with a deposition rate of {approximately}0.350 {mu}m/min onto a substrate at 330 C forming the anatase phase with < 1% residual C found in the final film. Compound 2 was found to sublime at 160 C and deposited as crystalline material at 300 C with < 1% residual C found in the final film. A comparison to standard alkoxide and {beta}-diketonates is presented where appropriate.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (US); Sandia National Labs., Livermore, CA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 9023
- Report Number(s):
- SAND99-1782J
- Journal Information:
- Advance Materials Chemical Vapor Deposition, Journal Name: Advance Materials Chemical Vapor Deposition
- Country of Publication:
- United States
- Language:
- English
Similar Records
Alkali metal yttrium neo-pentoxide double alkoxide precursors to alkali metal yttrium oxide nanomaterials
Synthesis and characterization of a series of Group 4 phenoxy-thiol derivatives