A comparative study of deformation in carbon/carbon and carbon/polyimide laminates under bi-axial compression
- Dartmouth College, Hanover, NH (United States). Thayer School of Engineering
The failure mechanisms of laminated 2-D carbon/carbon (C/C) and carbon/polyimide (C/P) composites have been determined under inplane biaxial compression loads, and the associated failure envelopes that account for the effect of matrix-type and loading directions, are also obtained. For the C/C laminates, the failure was in the form of micro-kinking of fiber-bundles, interspersed by localized interply delaminations to form the overall shear-fault. The shear fault was aligned with the major use of loading, except at above 75% of balanced biaxial stress, where failure occurred alone both axes. For the C/P laminates, however, the overall failure was primarily in the form of axial interply delaminations aligned with the principal axis of loading, with only secondary events of kinking in few bundles. Although the biaxial strength for both C/C and C/P samples varied significantly with the ratio of in-plane principal stresses, R, there was no variation in the local failure mechanisms. Accordingly, it was found that both materials fail upon achieving a maximum strain along the primary axis of loading.
- OSTI ID:
- 89862
- Report Number(s):
- CONF-9409291--; ISBN 1-56676-220-0
- Country of Publication:
- United States
- Language:
- English
Similar Records
Failure of woven carbon-polyimide laminates under off-axis compression loading
Failure mechanisms of laminated carbon-carbon composites; 2: Under shear loads