Method for making circular tubular channels with two silicon wafers

Patent · Sun Dec 31 23:00:00 EST 1995

OSTI ID:870689

Yu, Conrad M ^[1]; Hui, Wing C ^[2]

---

1. Antioch, CA
2. Campbell, CA

A two-wafer microcapillary structure is fabricated by depositing boron nitride (BN) or silicon nitride (Si.sub.3 N.sub.4) on two separate silicon wafers (e.g., crystal-plane silicon with [100] or [110] crystal orientation). Photolithography is used with a photoresist to create exposed areas in the deposition for plasma etching. A slit entry through to the silicon is created along the path desired for the ultimate microcapillary. Acetone is used to remove the photoresist. An isotropic etch, e.g., such as HF/HNO.sub.3 /CH.sub.3 COOH, then erodes away the silicon through the trench opening in the deposition layer. A channel with a half-circular cross section is then formed in the silicon along the line of the trench in the deposition layer. Wet etching is then used to remove the deposition layer. The two silicon wafers are aligned and then bonded together face-to-face to complete the microcapillary.

• Research Organization: Lawrence Livermore National Laboratory (LLNL), Livermore, CA
• DOE Contract Number: W-7405-ENG-48
• Assignee: Regents of University of California (Oakland, CA)
• Patent Number(s): US 5575929
• OSTI ID: 870689
• Country of Publication: United States
• Language: English

Related Subjects

/216/
100
110
acetone
aligned
bn
bonded
boron
boron nitride
channel
channels
circular
complete
cooh
create
created
crystal
crystal orientation
crystal-plane
depositing
deposition
desired
entry
erodes
etch
etching
exposed
fabricated
face-to-face
formed
half-circular
hf
hno
isotropic
layer
line
method
microcapillary
nitride
orientation
path
photolithography
photoresist
plasma
plasma etch
plasma etching
remove
section
separate
silicon
silicon nitride
silicon wafer
silicon wafers
slit
structure
trench
tubular
tubular channel
two-wafer
ultimate
wafers
wet
wet etching