Characteristics of laminates with delamination control strips
- McDonnell Aircraft Co., Saint Louis, MO (United States)
Tough resin is needed to resist delamination crack propagation. However, modulus often has to be compromised because it is difficult to retain both high modulus and toughness in a matrix material. A potential solution is to use a hybrid system in which tough resin strips are included within a conventional matrix composite. By adjusting the spacing of the tough resin strips, maximum delamination size can be controlled. Experimental results for impact damage and subsequent damage propagation in laminates containing tough resin strips are reported. Plain adhesive strips and fiber-reinforced tough resin composite strips were used in constructing the hybrid laminates. Test results indicated that size of delamination inflicted by impact was confined between the tough resin strips. As a result, significantly increased residual compressive strength was obtained. Impacted laminates containing tough resin strips were also fatigue tested. It was found that these strips reduced the growth of the impact damage area relative to the growth seen in coupons with no tough resin strips. Damage growth from an open hole under tension fatigue was evaluated using both tough resin strips and glass fiber reinforced tough resin strips. Unreinforced tough resin strips retarded delamination growth from the open hole, but did not stop matrix cracks growing in the fiber direction. Fiber reinforced tough resin strips did not contain axial delamination growth from the open hole. However, they did act as crack arresters, stopping the through-the-thickness tension crack originating from the hole.
- Research Organization:
- McDonnell Aircraft Co., St. Louis, MO (United States)
- OSTI ID:
- 79549
- Report Number(s):
- N--95-28420; NASA-CR--198723; NAS--1.26:198723; DOT/FAA/CT--92-25-VOL-1; CONF-9111350--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Composite materials: Fatigue and fracture; Proceedings of the Second Symposium, Cincinnati, OH, Apr. 27, 28, 1987. Volume 2
Creep-fatigue interaction in delamination crack propagation of advanced CFRPs at high temperatures