Final report. Defects and transport in mixed oxides
New results on the point defect chemistry of (Ni{sub x}Fe{sub 1-x}){sub 3-delta}O{sub 4} and on the cation tracer diffusion in this spinel solid solution are presented and discussed. The equation system for the defect chemistry of perovskites of the type A{sub 1-x}B{sub 1+x}O{sub 3-delta} have been worked out and used to derive Kr{umlt o}ger-Vink diagrams. The deviation from stoichiometry, delta, in LA{sub 1-x}Mn{sub 1+x}O{sub 3-delta} has been measured at 1100, 1200, and 1300 degrees Celsius as a function of the oxygen activity and the composition variable x. At high and low oxygen activities, the data were fit by taking into account the electrostatic interaction between the charge defects by making use of the Debye H{umlt u}ckel theory.
- Research Organization:
- Cornell University, Ithaca, NY (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- FG02-88ER45357
- OSTI ID:
- 771230
- Report Number(s):
- DOE/ER/45357--14
- Country of Publication:
- United States
- Language:
- English
Similar Records
Defects and transport in mixed oxides. Progress report, [December 22, 1992--September 30,1993]
Point defects and transport of matter and charge in non-stoichiometric oxides (II)
Defects and transport in mixed oxides. Progress report, October 1, 1993--December 20, 1994
Technical Report
·
Thu Sep 30 00:00:00 EDT 1993
·
OSTI ID:10169325
Point defects and transport of matter and charge in non-stoichiometric oxides (II)
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:518574
Defects and transport in mixed oxides. Progress report, October 1, 1993--December 20, 1994
Technical Report
·
Mon Dec 19 23:00:00 EST 1994
·
OSTI ID:29424