Recovery of lead after electron irradiation at 1. 5 K
Journal Article
·
· Phys. Rev., B; (United States)
The low-temperature recovery of lead following an electron irradiation at 1.5 K shows the same features observed for all face-centered-cubic metals except for gold. The stage I occurs below 5.5 K. The I/subD/ recovery substage occurs at 4.15 +- 0.05 K with an activation energy of 0.010 +- 0.001 eV. The I/subE/ substage shifts with defect concentration in lead as it does in copper. The I/subE/ activation energy is 0.010 +- 0.001 eV. Since platinum and lead anneal in stage I in the normal fashion, the strange behavior of gold is clearly not determined by its position in the periodic table. (AIP)
- Research Organization:
- Department of Physics and Materials Research Laboratory, University of Illinois, Urbana, Illinois 61801
- OSTI ID:
- 7365468
- Journal Information:
- Phys. Rev., B; (United States), Journal Name: Phys. Rev., B; (United States) Vol. 13:6; ISSN PLRBA
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stage-I recovery of prequenched and electron-irradiated pure aluminum and of the alloy Al-15 ppm Ag
STAGE I RECOVERY SPECTRUM OF PURE COPPER IRRADIATED WITH ELECTRONS OVER THE RANGE 1.25 TO 3.25 Mev
RECOVERY OF ELECTRON-IRRADIATED COPPER. I. CLOSE PAIR RECOVERY
Journal Article
·
Sun Feb 29 23:00:00 EST 1976
· J. Appl. Phys., v. 47, no. 3, pp. 809-816
·
OSTI ID:4006322
STAGE I RECOVERY SPECTRUM OF PURE COPPER IRRADIATED WITH ELECTRONS OVER THE RANGE 1.25 TO 3.25 Mev
Journal Article
·
Tue Dec 31 23:00:00 EST 1963
· Physical Review (U.S.) Superseded in part by Phys. Rev. A, Phys. Rev. B: Solid State, Phys. Rev. C, and Phys. Rev. D
·
OSTI ID:4152744
RECOVERY OF ELECTRON-IRRADIATED COPPER. I. CLOSE PAIR RECOVERY
Journal Article
·
Mon Jun 15 00:00:00 EDT 1959
· Physical Review (U.S.) Superseded in part by Phys. Rev. A, Phys. Rev. B: Solid State, Phys. Rev. C, and Phys. Rev. D
·
OSTI ID:4228485
Related Subjects
36 MATERIALS SCIENCE
360106* -- Metals & Alloys-- Radiation Effects
ANNEALING
BEAMS
CRYSTAL DEFECTS
CRYSTAL STRUCTURE
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELECTRON BEAMS
ELEMENTS
HEAT TREATMENTS
LEAD
LEPTON BEAMS
METALS
PARTICLE BEAMS
PHYSICAL PROPERTIES
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
ULTRALOW TEMPERATURE
360106* -- Metals & Alloys-- Radiation Effects
ANNEALING
BEAMS
CRYSTAL DEFECTS
CRYSTAL STRUCTURE
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELECTRON BEAMS
ELEMENTS
HEAT TREATMENTS
LEAD
LEPTON BEAMS
METALS
PARTICLE BEAMS
PHYSICAL PROPERTIES
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
ULTRALOW TEMPERATURE