Textures of laser ablated superconducting thin films of YBa sub 2 Cu sub 3 O sub 7 minus. delta. as a function of deposition temperature

Journal Article · Sat Feb 29 23:00:00 EST 1992 · Journal of Materials Research; (United States)

DOI:https://doi.org/10.1557/JMR.1992.0549· OSTI ID:7306503

Heidelbach, R; Wenk, H ^[1]; Muenchausen, R E; Foltyn, S; Nogar, N ^[2]; Rollett, A D ^[3]

---

1. Department of Geology and Geophysics, University of California, Berkeley, California 94720 (United States) Center for Materials Science, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)
2. Exploratory Research and Development Center, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)
3. Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)

The preferred orientation of a series of laser deposited superconducting thin films of YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} on LaAlO{sub 3} substrate has been examined. X-ray measurements (pole figures, {chi}-scans, {omega}-scans, rocking curves) reveal an increasingly strong preferred orientation of the polycrystalline material with c-axes perpendicular to the substrate surface as deposition temperature increases. At low temperatures c-axes are predominantly parallel to the substrate surface. Characteristic parameters of the texture types were derived from those measurements. With higher temperatures twinning on (110) was observed. The different texture types are interpreted in terms of a layered film structure.

• OSTI ID: 7306503
• Journal Information: Journal of Materials Research; (United States), Journal Name: Journal of Materials Research; (United States) Vol. 7:3; ISSN JMREE; ISSN 0884-2914
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
ALKALINE EARTH METAL COMPOUNDS
AMINES
AMMONIUM COMPOUNDS
BARIUM COMPOUNDS
BARIUM OXIDES
CHALCOGENIDES
COHERENT SCATTERING
COPPER COMPOUNDS
COPPER OXIDES
CRYSTALS
DEPOSITION
DIFFRACTION
ELECTROMAGNETIC RADIATION
FILMS
HIGH-TC SUPERCONDUCTORS
LASER RADIATION
ORGANIC COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
POLYCRYSTALS
QUATERNARY COMPOUNDS
RADIATIONS
SCATTERING
SUPERCONDUCTORS
TEMPERATURE DEPENDENCE
TEXTURE
THIN FILMS
TRANSITION ELEMENT COMPOUNDS
X-RAY DIFFRACTION
YTTRIUM COMPOUNDS
YTTRIUM OXIDES