Evolution of porosity and calcium hydroxide in laboratory concretes containing silica fume
- National Inst. of Standards and Technology, Gaithersburg, MD (United States). Building and Fire Research Lab.
Laboratory concretes containing only coarse aggregates and 0, 10, or 20% silica fume as a cement replacement were prepared at a constant water-to-solids ratio and sampled at 1, 7, and 28 days. Scanning electron microscopy was utilized to monitor the progress of the hydration reactions both in the bulk paste and in regions near an aggregate surface. Phase volume fractions were determined by quantitative image analysis of the backscattered electron images. In addition, the size of individual'' two-dimensional cross sections of calcium hydroxide crystals and capillary pores were assessed. Silica fume additions are seen to affect both the amount and size of these microstructural features. Differences are observed between interfacial zone and bulk areas which support previous mercury intrusion measurements of mortar specimens. This analysis lends support to the hypothesis that when silica fume is present, calcium hydroxide crystals form and then dissolve away, contributing to a connected pathway of capillary porosity in the interfacial zone regions.
- OSTI ID:
- 7152983
- Journal Information:
- Cement and Concrete Research; (United States), Journal Name: Cement and Concrete Research; (United States) Vol. 24:6; ISSN 0008-8846; ISSN CCNRAI
- Country of Publication:
- United States
- Language:
- English
Similar Records
Percolation and pore structure in mortars and concrete
Application of nanoindentation testing to study of the interfacial transition zone in steel fiber reinforced mortar
Related Subjects
320305 -- Energy Conservation
Consumption
& Utilization-- Industrial & Agricultural Processes-- Industrial Waste Management
36 MATERIALS SCIENCE
360602* -- Other Materials-- Structure & Phase Studies
ALKALINE EARTH METAL COMPOUNDS
ASHES
BENCH-SCALE EXPERIMENTS
BUILDING MATERIALS
CALCIUM COMPOUNDS
CALCIUM HYDROXIDES
CHALCOGENIDES
COMBUSTION PRODUCTS
CONCRETES
CRYSTAL GROWTH
DISSOLUTION
HYDROGEN COMPOUNDS
HYDROXIDES
MATERIALS
MICROSTRUCTURE
OXIDES
OXYGEN COMPOUNDS
PORE STRUCTURE
RESIDUES
SILICON COMPOUNDS
SILICON OXIDES
WASTE PRODUCT UTILIZATION