Performance of 9 to 12% Cr-1 Mo steels during flattening test
The performance of modified 9 Cr-1 Mo, HT9, and types 316 and 321 stainless steel in the ASTM flattening test (A 530) is reported. The modified 9 Cr-1 Mo tubes tested were made by centrifugal casting and cold pilgering and by hot extrusion. The modified 9 Cr-1 Mo and HT9 were tested in the normalized and tempered condition and after aging for 3000 h at 482, 538, 593, 649, and 704{sup 0}C. Both alloys were also tested in the welded condition. Type 316 stainless steel was tested in the mill-annealed condition. Type 321 was tested as removed from the superheater section of the TVA Kingston power plant and after solution annealing.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-26
- OSTI ID:
- 706510
- Report Number(s):
- ORNL/TM--7698
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanical properties of structural materials for FBR sodium application. Semi-annual progress report for period ending January 31, 1982
Time-Dependent Properties of Welds in Type 316 Stainless Steel Formed-and-Welded Pipes
Mechanical properties test data for structural materials. Semiannual progress report for period ending July 31, 1980
Technical Report
·
Thu Dec 31 23:00:00 EST 1981
·
OSTI ID:5277366
Time-Dependent Properties of Welds in Type 316 Stainless Steel Formed-and-Welded Pipes
Technical Report
·
Mon Sep 01 00:00:00 EDT 1980
·
OSTI ID:1811399
Mechanical properties test data for structural materials. Semiannual progress report for period ending July 31, 1980
Technical Report
·
Mon Dec 31 23:00:00 EST 1979
·
OSTI ID:5256553