Conducting polymers and corrosion: Polyaniline on steel
- North Dakota State Univ., Fargo, ND (United States)
Polyaniline-coated steel panels were studied by electrochemical impedance spectroscopy (EIS) and electrochemical noise methods (ENM). EIS data for the polyaniline sample was obtained for increasing time of immersion. An increase in charge-transfer resistance (R{sub ct}) with immersion time was observed. ENM data showed that active electrochemical changes occurred during the early stages of immersion. The mean current from ENM exhibited a rather large oscillatory behavior during early stages of immersion, and the mean potential from ENM displayed a tendency toward positive values. Noise resistance (R{sub n}) values also showed initial oscillatory fluctuations, with values that reflected a poor barrier property for polyaniline coating. Tafel plots showed a lower corrosion rate and a more noble corrosion potential for the polyaniline-coated sample as compared to a bare steel sample. Electrochemical data confirmed that significant interactions between the polyaniline and steel occurred during he first 5 days of immersion, but that a continuing interaction occurred throughout the entire immersion period. EIS of a polyaniline/epoxy two-coated system on steel also was carried out. Performance of the polyaniline/epoxy system was superior to that of bare steel coated with epoxy alone.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 684434
- Journal Information:
- Corrosion, Journal Name: Corrosion Journal Issue: 8 Vol. 55; ISSN 0010-9312; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electrochemical studies of corrosion inhibiting effect of polyaniline coatings
Corrosion protection mechanism of polyaniline blended organic coating on steel