Dependence of critical current density on filament diameter in round multifilament Ag-sheathed Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub [ital x]] wires processed in O[sub 2]
Journal Article
·
· Applied Physics Letters; (United States)
- IGC Advanced Superconductors, Waterbury, Connecticut 06704 (United States)
- University of Wisconsin, Madison, Wisconsin 53706 (United States)
Ag-sheathed Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub [ital x]] round wires having 37 and 259 filaments, with filament diameters ranging from 11 to 100 [mu]m, were fabricated by the oxide-powder-in-tube method. They were heat treated using step-solidification melt processing in air and pure O[sub 2]. The transport critical current density was highest in wires processed in pure O[sub 2]. It increased with decreasing filament diameter and was highest [165 000 A/cm[sup 2] (4.2 K, O T)] in wires with 11 [mu]m filaments processed in O[sub 2].
- DOE Contract Number:
- FG02-92ER81461
- OSTI ID:
- 6802991
- Journal Information:
- Applied Physics Letters; (United States), Vol. 65:21; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Processing and properties of BSCCO 2212 Ag and Ag alloy multifilament round wires
Quench degradation limit of multifilamentary AgBi2Sr2CaCu2Ox round wires
Strain control of composite superconductors to prevent degradation of superconducting magnets due to a quench: I. Ag/Bi2Sr2CaCu2Ox multifilament round wires
Journal Article
·
Sun Jun 01 00:00:00 EDT 1997
· Advances in Cryogenic Engineering
·
OSTI ID:6802991
Quench degradation limit of multifilamentary AgBi2Sr2CaCu2Ox round wires
Journal Article
·
Tue Feb 02 00:00:00 EST 2016
· Superconductor Science and Technology
·
OSTI ID:6802991
+1 more
Strain control of composite superconductors to prevent degradation of superconducting magnets due to a quench: I. Ag/Bi2Sr2CaCu2Ox multifilament round wires
Journal Article
·
Thu Dec 01 00:00:00 EST 2016
· Superconductor Science and Technology
·
OSTI ID:6802991
+2 more
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
36 MATERIALS SCIENCE
BISMUTH OXIDES
CRITICAL CURRENT
CALCIUM OXIDES
COPPER OXIDES
HIGH-TC SUPERCONDUCTORS
STRONTIUM OXIDES
SUPERCONDUCTING WIRES
FABRICATION
FILAMENTS
HEAT TREATMENTS
MICROSTRUCTURE
TEXTURE
ALKALINE EARTH METAL COMPOUNDS
BISMUTH COMPOUNDS
CALCIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
CURRENTS
ELECTRIC CURRENTS
OXIDES
OXYGEN COMPOUNDS
STRONTIUM COMPOUNDS
SUPERCONDUCTORS
TRANSITION ELEMENT COMPOUNDS
WIRES
665412* - Superconducting Devices- (1992-)
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360207 - Ceramics
Cermets
& Refractories- Superconducting Properties- (1992-)
SUPERCONDUCTIVITY AND SUPERFLUIDITY
36 MATERIALS SCIENCE
BISMUTH OXIDES
CRITICAL CURRENT
CALCIUM OXIDES
COPPER OXIDES
HIGH-TC SUPERCONDUCTORS
STRONTIUM OXIDES
SUPERCONDUCTING WIRES
FABRICATION
FILAMENTS
HEAT TREATMENTS
MICROSTRUCTURE
TEXTURE
ALKALINE EARTH METAL COMPOUNDS
BISMUTH COMPOUNDS
CALCIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
CURRENTS
ELECTRIC CURRENTS
OXIDES
OXYGEN COMPOUNDS
STRONTIUM COMPOUNDS
SUPERCONDUCTORS
TRANSITION ELEMENT COMPOUNDS
WIRES
665412* - Superconducting Devices- (1992-)
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360207 - Ceramics
Cermets
& Refractories- Superconducting Properties- (1992-)