Cathodoluminescence spectroscopy of deep defect levels at the ZnSe/GaAs interface with a composition-control interface layer
- Ohio State Univ., Columbus, OH (United States)
- Lab. Nazionale TASC-INFM, Trieste (Italy)
In this work the authors investigate ZnSe/GaAs heterostructures with an additional 2 nm controlled interfacial layer (CIL) of Se- or Zn-rich composition to modify the band offset. The samples are analyzed as a function of annealing temperature by cathodoluminescence spectroscopy. The as-prepared samples show defect luminescence at {approximately}0.9 eV. With staged annealing at increasing temperatures, both the Zn-rich as well as the Se-rich interfacial layer exhibits luminescence at {approximately}1.9 eV, indicative of defect formation with an onset temperature of {approximately}400 C. Excitation-dependent spectroscopy provides evidence for defect formation near the interface, which extends into the ZnSe epilayer at higher temperatures. Compared to earlier work, where the threshold temperature for defect formation in bulk samples fabricated under Se-rich growth conditions occurs at temperatures as low as 325 C, the resistance to defect formation has now been improved to that of stoichiometric ZnSe. These results demonstrate that epitaxially grown CILs provide a means to alter ZnSe/GaAs band offsets without degrading the heterojunction`s resistance to defect formation at elevated temperatures.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 679208
- Journal Information:
- Journal of Electronic Materials, Journal Name: Journal of Electronic Materials Journal Issue: 7 Vol. 28; ISSN JECMA5; ISSN 0361-5235
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of Tl related centers on ZnSe radiation spectra
An x-ray photoelectron spectroscopy study of bonding at II-VI/III-V heterovalent interfaces