Highly oriented as-deposited superconducting laser ablated thin films of Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub 7-//sub delta/ on SrTiO/sub 3/, zirconia, and Si substrates
KrF excimer laser ablation of an Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub 7-//sub delta/ pellet in 0.1--0.2 Torr of O/sub 2/ ambient was used to deposit thin superconducting films onto SrTiO/sub 3/, yttria-stabilized zirconia (YSZ), and silicon substrates at 600--700 /sup 0/C. The as-deposited 1-..mu..m-thick films at 650--700 /sup 0/C substrate temperature were superconducting, without further high-temperature annealing. All films had a similar T/sub c/ onset of approx.92 K but different zero-resistance T/sub c/ of 90, 85, and 70 K for the films on SrTiO/sub 3/, YSZ, and Si substrates, respectively. Angular x-ray diffraction analysis showed that all the films were highly oriented with the c axis perpendicular to their surface. Critical current densities at 77 K were about 40 000 and 10 000 A/cm/sup 2/ for the films on SrTiO/sub 3/ and YSZ, respectively. Smooth surface morphology was observed in all films, with occasional defects and cracks in the films on YSZ, which seems to explain the lower critical current in these films.
- Research Organization:
- Physics Department, Technion-Israel Institute of Technology, Haifa 32000, Israel
- OSTI ID:
- 6711540
- Journal Information:
- Appl. Phys. Lett.; (United States), Journal Name: Appl. Phys. Lett.; (United States) Vol. 53:23; ISSN APPLA
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ single chamber laser processing of YBa sub 2 Cu sub 3 O sub 7 minus. delta. superconducting thin films on Si (100) with yttria-stabilized zirconia buffer layers
In situ processing of epitaxial Y-Ba-Cu-O high T/sub c/ superconducting films on (100) SrTiO/sub 3/ and (100) YS-ZrO/sub 2/ substrates at 500--650 /sup 0/C
Related Subjects
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
360204 -- Ceramics
Cermets
& Refractories-- Physical Properties
656100 -- Condensed Matter Physics-- Superconductivity
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABLATION
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
BARIUM OXIDES
CHALCOGENIDES
COATINGS
COHERENT SCATTERING
COPPER COMPOUNDS
COPPER OXIDES
CRITICAL CURRENT
CURRENT DENSITY
CURRENTS
DATA
DEPOSITION
DIFFRACTION
DIMENSIONS
ELECTRIC CURRENTS
ELECTROMAGNETIC RADIATION
ELEMENTS
EXPERIMENTAL DATA
FABRICATION
FILMS
INFORMATION
LASER RADIATION
LOW TEMPERATURE
MORPHOLOGY
NUMERICAL DATA
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
RADIATIONS
SCATTERING
SEMIMETALS
SILICON
STRONTIUM COMPOUNDS
STRONTIUM OXIDES
SUPERCONDUCTING FILMS
SURFACE COATING
THERMODYNAMIC PROPERTIES
THICKNESS
THIN FILMS
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS
TRANSITION TEMPERATURE
VAPOR DEPOSITED COATINGS
VERY HIGH TEMPERATURE
X-RAY DIFFRACTION
YTTRIUM COMPOUNDS
YTTRIUM OXIDES
ZIRCONIUM COMPOUNDS
ZIRCONIUM OXIDES