Matrix phase in ceramics with composition near BaO. Nd/sub 2/O/sub 3/. 5TiO/sub 2/

Journal Article · Wed Oct 01 04:00:00 EDT 1986 · J. Am. Ceram. Soc.; (United States)

OSTI ID:6656502

Jaakola, T; Uusimaki, A; Rautioaho, R; Leppavuori, S

Phase structures of two ceramics of compositions BaNd/sub 2/Ti/sub 5/O/sub 14/ and Ba/sub 3.75/Nd/sub 9.5/Ti/sub 18/O/sub 54/, both of which had earlier been reported to be single-phase materials, were investigated using electron microscopy and an electron probe microanalyzer. It was observed that the amount of secondary phases was much lower in ceramics prepared with the latter composition and that the composition of the matrix phase of both samples was near 4BaO . 5Nd/sub 2/O/sub 3/ . 18TiO/sub 2/.

• Research Organization: Dept. of Electrical Engineering, Univ. of Oulu, SF-90570 Oulu
• OSTI ID: 6656502
• Journal Information: J. Am. Ceram. Soc.; (United States), Journal Name: J. Am. Ceram. Soc.; (United States) Vol. 69:10; ISSN JACTA
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
360202 -- Ceramics
Cermets
& Refractories-- Structure & Phase Studies
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
400102 -- Chemical & Spectral Procedures
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
BARIUM OXIDES
CERAMICS
CHALCOGENIDES
CHEMICAL COMPOSITION
CHEMICAL PREPARATION
CRYSTAL STRUCTURE
CRYSTAL-PHASE TRANSFORMATIONS
CRYSTALS
DISPERSIONS
ELECTRON MICROSCOPY
EXPERIMENT PLANNING
MICROSCOPY
MICROSTRUCTURE
MIXTURES
MONOCRYSTALS
NEODYMIUM COMPOUNDS
NEODYMIUM OXIDES
OXIDES
OXYGEN COMPOUNDS
PHASE TRANSFORMATIONS
PLANNING
POWDERS
RARE EARTH COMPOUNDS
STRUCTURAL CHEMICAL ANALYSIS
SYNTHESIS
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS