Investigation of the aluminium-rich corner in the Al-Si-W phase diagram
Journal Article
·
· Scripta Metallurgica et Materialia
- K.U. Leuven, Heverlee (Belgium). Dept. Metallurgy and Materials Engineering
In the present work the Al-rich corner of the Al-Si system with the refractory metal W was investigated at 1000 C. The information available for this ternary system refers to 1,500 C and to higher Si-and W-contents. The phases which had formed after holding at 1,000 C were used to construct an isothermal section of the phase diagram at this temperature. Also the compounds which precipitate from the Al-melt during cooling are described. Possible applications of the alloys are discussed.
- OSTI ID:
- 64367
- Journal Information:
- Scripta Metallurgica et Materialia, Journal Name: Scripta Metallurgica et Materialia Journal Issue: 9 Vol. 32; ISSN SCRMEX; ISSN 0956-716X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Titanium corner of the Ti--Al--W phase diagram
Phase relationships in Cu-rich corner of the Cu-Cr-Zr phase diagram
DETERMINATION OF THE NIOBIUM-RICH REGION OF THE TERNARY PHASE DIAGRAMS, NIOBIUM-TUNGSTEN-HAFNIUM AND NIOBIUM-TUNGSTEN-ZIRCONIUM. Quarterly Report No. 2, December 1, 1962 to March 1, 1963
Journal Article
·
Sun Dec 31 23:00:00 EST 1972
· Izv. Akad. Nauk SSSR, Metal., no. 3, pp. 218-223
·
OSTI ID:4326165
Phase relationships in Cu-rich corner of the Cu-Cr-Zr phase diagram
Journal Article
·
Thu Jun 15 00:00:00 EDT 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:92970
DETERMINATION OF THE NIOBIUM-RICH REGION OF THE TERNARY PHASE DIAGRAMS, NIOBIUM-TUNGSTEN-HAFNIUM AND NIOBIUM-TUNGSTEN-ZIRCONIUM. Quarterly Report No. 2, December 1, 1962 to March 1, 1963
Technical Report
·
Thu Feb 28 23:00:00 EST 1963
·
OSTI ID:4752893