Texture and yield stress of pre-strained 304L stainless steel
The evolution of texture and yield stress in 304L stainless steel is investigated as a function of deformation to large plastic strains. Steel bars quasi-statically upset forged at a strain rate of 0.001 s{sup {minus}1} to true strains of 0, 0.5, 1.0 and 1.8 were found to acquire their texture ({approximately}3.0 m.r.d.) in the first 0.5 strain with (110) poles highly aligned parallel to the compression direction independent of whether the pre-forged starting material was in a cold worked or annealed (1,050 C for 1 hour) condition. The same bars, when strained at room temperature show an incremental yield with pre-strain regardless of strain rate (10{sup {minus}1} or 10{sup {minus}3}s{sup {minus}1}) or thermal history, though annealed bars yield at slightly lower stresses. At 77 K and strain rate 10{sup {minus}3}s{sup {minus}1}, the annealed 304L exhibits more pronounced strain-hardening behavior than the 304L forged in a cold-worked condition.
- Research Organization:
- Los Alamos National Lab., NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 638212
- Report Number(s):
- LA-UR--98-686; CONF-9706260--; ON: DE98003708
- Country of Publication:
- United States
- Language:
- English
Similar Records
Texture and Yield Stress of Pre-Strained 304L Stainless Steel
Forging evaluaion of 304L stainless steel
Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates
Conference
·
Mon Jun 23 00:00:00 EDT 1997
·
OSTI ID:762581
Forging evaluaion of 304L stainless steel
Technical Report
·
Sun Oct 28 23:00:00 EST 1979
·
OSTI ID:5764455
Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates
Journal Article
·
Thu Dec 31 19:00:00 EST 2020
· Mechanics of Materials
·
OSTI ID:1769892