High-temperature fracture and fatigue resistance of a ductile {beta}-TiNb reinforced {gamma}-TiAl intermetallic composite

Journal Article · Fri Jul 24 04:00:00 EDT 1998 · Acta Materialia

OSTI ID:634662

Rao, K T.V. ^[1]; Ritchie, R O ^[2]

---

1. Guidant Corp., Santa Clara, CA (United States). Advanced Cardiovascular Systems
2. Univ. of California, Berkeley, CA (United States). Dept. of Materials Science and Mineral Engineering

The high-temperature fatigue-crack propagation and fracture resistance of a model {gamma}-TiAl intermetallic composite reinforced with 20 vol. % ductile {beta}-TiNb particles is examined at elevated temperatures of 650 and 800 C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of {gamma}-TiAl, even at high temperatures, from about 123 to {approximately}40 MPa m{sup {1/2}}, although their effectiveness is lower compared to room temperature due to the reduction in strength of TiNb particles. Under monotonic loading, crack-growth response in the composite is characterized by resistance-curve behavior arising from crack trapping, renucleation and resultant crack bridging effects attributable to the presence of TiNb particles. In addition, crack-tip blunting associated with plasticity increases the crack-initiation (matrix) toughness of the composite, particularly at 800 C, above the ductile-to-brittle transition temperature (DBTT) for {gamma}-TiAl. High-temperature fatigue-crack growth resistance, however, is marginally degraded by the addition of TiNb particles in the C-R (edge) orientation, similar to observations made at room temperature; premature fatigue failure of TiNb ligaments in the crack wake diminishes the role of bridging under cyclic loading. Both fatigue and fracture resistance of the composite are slightly lower at 650 C (just below the DBTT for TiAl) compared to the behavior at ambient and 800 C. Overall, the beneficial effect of adding ductile TiNb reinforcements to enhance the room-temperature fracture and fatigue resistance of {gamma}-TiAl alloys is retained up to 800 C, in air environments. There is concern, however, regarding the long-term environmental stability of these composite microstructures in unprotected atmospheres.

• OSTI ID: 634662
• Journal Information: Acta Materialia, Journal Name: Acta Materialia Journal Issue: 12 Vol. 46; ISSN 1359-6454; ISSN ACMAFD
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
COMPOSITE MATERIALS
CRACK PROPAGATION
FATIGUE
FRACTURE PROPERTIES
INTERMETALLIC COMPOUNDS
NIOBIUM ALLOYS
TEMPERATURE DEPENDENCE
TITANIUM ALLOYS