Fracture toughness of Al/sub 2/O/sub 3/-ZrO/sub 2/ composites
K/sub IC/ of Al/sub 2/O/sub 3/-ZrO/sub 2/ two-phase ceramic composites was determined for different ZrO/sub 2//Al/sub 2/O/sub 3/ ratios and selected Y/sub 2/O/sub 3/ stabilizer concentrations in the ZrO/sub 2/. The double cantilver beam (DCB) specimen geometry was used. In composites containing 20 vol % ZrO/sub 2/, K/sub IC/ increases (4.6 to 8.5 MPa m/sup 1/2/) with decrease in Y/sub 2/O/sub 3/ content from 3 to 1 mol %. On the other hand, composites containing 30 vol % ZrO/sub 2/, decreasing Y/sub 2/O/sub 3/ additions from 3 to 2 mol % leads to a maximum in K/sub IC/ value of about 6.2 MPa m/sup 1/2/ which occurred in a composition containing 2 mol % Y/sub 2/O/sub 3/. In this same composite, this maximum shifts to a value of about 8 MPa m/sup 1/2/ at about 2 to 3 mol % Y/sub 2/O/sub 3/ at -195/sup 0/C. These observations are consistent with a transformation toughening model wherein an increase in toughness occurs with decrease in Y/sub 2/O/sub 3/ content due to a decrease in the chemical free energy required for the transformation of tetragonal ZrO/sub 2/ to the monoclinic form. The K/sub IC/ also exhibits a maximum with the concentration of ZrO/sub 2/ particles and this maximum in K/sub IC/ increases in value and shifts to higher ZrO/sub 2/ contents wih Y/sub 2/O/sub 3/ stabilizer concentrations of 2 mol %. The increase in K/sub IC/ with ZrO/sub 2/ content results from the resultant increase in the number of ZrO/sub 2/ particles which transform to the monoclinic phase during crack propagation. Microstructural analyses indicate the preexisting extended microcracks are produced along the alumina grain boundaries when larger ZrO/sub 2/ particles at the boundaries transform to the monoclinic phase during cooling subsequent to densification. Such extended microcracking results in a reduction of toughening when linking of microcracks occurs. Microcracks also form at the intersection of ZrO/sub 2/ transformation twins within the particles and the ZrO/sub 2/ particle interface with other ZrO/sub 2/ grains or Al/sub 2/O/sub 3/ grains.
- Research Organization:
- Oak Ridge National Lab., TN (USA)
- DOE Contract Number:
- W-7405-ENG-26
- OSTI ID:
- 6346173
- Report Number(s):
- CONF-810746-1; ON: DE81028575
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of aqueous processing conditions on the microstructure and transformation behavior in Al[sub 2]O[sub 3]-ZrO[sub 2](CeO[sub 2]) composites
Fracture toughness of Al{sub 2}O{sub 3}-particle-dispersed Y{sub 2}O{sub 3}-partially stabilized zirconia
Related Subjects
360203* -- Ceramics
Cermets
& Refractories-- Mechanical Properties
ALUMINIUM COMPOUNDS
ALUMINIUM OXIDES
CHALCOGENIDES
CHEMICAL COMPOSITION
COMPOSITE MATERIALS
CRACK PROPAGATION
CRYSTAL STRUCTURE
DISPERSIONS
FRACTURE PROPERTIES
MATERIALS
MECHANICAL PROPERTIES
MICROSTRUCTURE
MIXTURES
OXIDES
OXYGEN COMPOUNDS
PHASE TRANSFORMATIONS
TRANSITION ELEMENT COMPOUNDS
YTTRIUM COMPOUNDS
YTTRIUM OXIDES
ZIRCONIUM COMPOUNDS
ZIRCONIUM OXIDES