The electronic transport mechanism in amorphous tetrahedrally-coordinated carbon films
The electronic transport mechanism in tetrahedrally coordinated amorphous carbon was investigated using measurements of stress relaxation, thermal evolution of electrical conductivity, and temperature dependent conductivity measurements. Stress relaxation measurements were used to determine the change in 3-fold coordinated carbon concentration, and the electrical conductivity was correlated to this change. It was found that the conductivity was exponentially proportional to the change in 3-fold concentration, indicating a tunneling or hopping transport mechanism. It was also found that the activation energy for transport decreased with increasing anneal temperature. The decrease in activation energy was responsible for the observed increase in electrical conductivity. A model is described wherein the transport in this material is described by thermally activated conduction along 3-fold linkages or chains with variable range and variable orientation hopping. Thermal annealing leads to chain ripening and a reduction in the activation energy for transport.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 634073
- Report Number(s):
- SAND--97-1673C; CONF-971201--; ON: DE98003136; BR: DP0301010
- Country of Publication:
- United States
- Language:
- English
Similar Records
Pressure-induced amorphization of a dense coordination polymer and its impact on proton conductivity
Preparation and electrical properties of LaCr/sub 1-//sub x/Cu/sub x/O/sub 3/