Parametric testing of a DWPF glass
A series of tests has been performed to characterize the chemical stability of a DWPF borosilicate glass sample as part of the Waste Package Task of the Nevada Nuclear Waste Storage Investigations (NNWSI) Project. This material was prepared at the Savannah River Laboratory for the purpose of testing the 165-frit matrix doped with a simulated nonradioactive waste. All tests were conducted at 90{sup 0}C using deionized water and J-13 water (a tuffaceous formation ground water). In the deionized water tests, both monoliths and crushed glass were tested at various ratios of surface area of the sample to volume of water in order to compare leach rates for different sample geometries or leaching times. Effects on the leach rates as a result of the presence of crushed tuff and stainless steel material were also investigated in the tests with J-13 water. 3 refs., 12 figs., 7 tabs.
- Research Organization:
- Lawrence Livermore National Lab., CA (United States)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 59362
- Report Number(s):
- UCRL--53606; ON: DE85015087
- Country of Publication:
- United States
- Language:
- English
Similar Records
Parametric testing of a DWPF borosilicate glass
Leach tests at Savannah River Laboratory for radioactive and nonradioactive nuclear waste glasses