Parametric testing of a DWPF borosilicate glass
A series of tests have been performed to characterize the chemical stability of a DWPF borosilicate glass sample as part of the Waste Package Task of the NNWSI Project. This material was prepared at the Savannah River Laboratory for the purpose of testing the 165-frit matrix doped with a simulated non-radioactive waste. All tests were conducted at 90{sup 0}C using deionized water and J-13 water (a tuffaceous formation groundwater). In the deionized water tests, both monoliths and crushed glass were tested at various ratios of surface area of the sample to volume of water in order to compare leach rates for different sample geometries or leaching times. Effects on the leach rates due to the presence of crushed tuff and stainless steel material were also investigated in the tests with J-13 water. 4 references, 2 figures, 4 tables.
- Research Organization:
- Lawrence Livermore National Lab., CA (United States)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 59355
- Report Number(s):
- UCRL--90857; CONF-841157--80; ON: DE85007254
- Country of Publication:
- United States
- Language:
- English
Similar Records
Parametric testing of a DWPF glass
Development of a nuclear waste glass product consistency test