Corrosion evaluation of aluminum 5083
Technical Report
·
OSTI ID:5922959
The results from the ASSET (exfoliation), NAWLT (weight loss after exposure to nitric acid), and stress corrosion cracking tests of aluminum 5083 used in pressure vessels are presented. Most of the corrosion work was done on commercial plate stock material from a process developed at Lawrence Livermore National Laboratory (LLNL), although some hemispheres (hemis) from both commercial and premium grade material were used in the ASSET evaluation. The hemis from commercial aluminum experienced severe exfoliation corrosion, while the premium material was left virtually unattacked.
- Research Organization:
- Lawrence Livermore National Lab., CA (USA)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 5922959
- Report Number(s):
- UCRL-53387; ON: DE83015786
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evaluation of the corrosion properties of aluminum alloy 5083 weldments
Stress corrosion testing of 5083 aluminum
Superplastic behavior in a commercial 5083 aluminum alloy
Technical Report
·
Sun Nov 04 23:00:00 EST 1984
·
OSTI ID:6059598
Stress corrosion testing of 5083 aluminum
Journal Article
·
Sat Aug 01 00:00:00 EDT 1981
· Corrosion (Houston); (United States)
·
OSTI ID:5488016
Superplastic behavior in a commercial 5083 aluminum alloy
Journal Article
·
Mon Feb 28 23:00:00 EST 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:5227799