Stress corrosion testing of 5083 aluminum
The stress corrosion susceptibility of thermomechanically processed 5083 aluminum-magnesium alloy was determined in a 3.5 Wt% sodium chloride environment. Alternate immersion C-ring and constant elongation rate tensile tests were performed. Comparison of the test results indicated that both techniques revealed the susceptibility of short transverse specimens to stress corrosion cracking. Potentiokinetic determinations of the characteristic pitting potential (Ep) and protection potential (Epp), were made. In deaerated 3.5 Wt% sodium chloride, Ep is -740 mV and Epp is -770 mV versus a standard calomel reference electrode. Standard tensile tests (air environment) were also conducted to generate base line strength data. The short transverse tensile specimens had a nominal 260 MPa (38 ksi) yield strength and 6.5% total elongation. Comparison of base line data with the stress corrosion data revealed that constant elongation rate test results are dependent upon a balance of normal ductile failure and the corrosion induced failure modes. Impressed potentials equal to or more noble than the pitting potential (Ep) generated the maxium degradation of mechanical properties while impressed potentials more negative than the protection potential (Epp) did not alter the mechanical properties of 5083 aluminum. Thus, the development of constant elongation rate tensile tests required an in-depth understanding of the corrosion mechanisms and the mechanical properties of 5083 aluminum. Alternate immersion C-ring tests generated specimen pass or fail information which indicated susceptibility of staticly loaded (80% of yield) specimens to stress corrosion induced failure. Tests results showed that only four of eight specimens tested contained stress corrosion failures.
- Research Organization:
- Los Alamos Scientific Lab., NM
- OSTI ID:
- 5488016
- Journal Information:
- Corrosion (Houston); (United States), Journal Name: Corrosion (Houston); (United States) Vol. 37:8; ISSN CORRA
- Country of Publication:
- United States
- Language:
- English
Similar Records
The stress corrosion resistance and the cryogenic temperature mechanical properties of annealed Nitronic 60 bar material
Mechanical properties of SP 5083 aluminum after superplastic forming
Related Subjects
360105* -- Metals & Alloys-- Corrosion & Erosion
ALKALI METAL COMPOUNDS
ALLOYS
ALUMINIUM ALLOYS
ALUMINIUM BASE ALLOYS
CHEMICAL REACTIONS
CHLORIDES
CHLORINE COMPOUNDS
CORROSION
CRACK PROPAGATION
HALIDES
HALOGEN COMPOUNDS
MAGNESIUM ALLOYS
MATERIALS TESTING
SODIUM CHLORIDES
SODIUM COMPOUNDS
STRESS ANALYSIS
STRESS CORROSION
TESTING