Steel bars, forgings, and rings 0.50Cr 0.55Ni 0.25Mo (0.38-0.43c) (reaffirmed, 1992). (SAE standard)
Technical Report
·
OSTI ID:591033
Primarily for parts with section thickness of 0.375 in. (9.52 mm) and under at the time of heat treatment, requiring a through-hardening steel capable of developing hardness as high as 50 HRC when properly hardened and tempered and also parts of greater thickness but requiring proportionately lower hardness. Alloy: 8740 UNS Number: G8740.
- Research Organization:
- Society of Automotive Engineers, Inc., Warrendale, PA (United States)
- OSTI ID:
- 591033
- Report Number(s):
- SAE-AMS-6322K/XAB; TRN: 80903327
- Resource Relation:
- Other Information: DN: DoDISS Adopted. Copyright Society for Automotive Engineers (SAE), 400 Commonwealth Drive, Warrendale, PA. 15096, USA. This document is available from NTIS under license from SAE. See also MIL-S-6049; PBD: Jan 1987
- Country of Publication:
- United States
- Language:
- English
Similar Records
Steel, bars, forgings, and tubing 0.80Cr 1.8Ni 0.25Mo (0.38-0.43C) special aircraft quality cleanliness, normalized and tempered. (SAE standard)
Steel, bars, forgings, and tubing, 0.80Cr 1.8Ni 0.25Mo (0.38 0.43c). (SAE standard)
Steel bars, forgings and rings, 0.95Cr 0.20Mo (0.38-0.43C), annealed. (SAE standard)
Technical Report
·
Sat Jun 01 00:00:00 EDT 1996
·
OSTI ID:591033
Steel, bars, forgings, and tubing, 0.80Cr 1.8Ni 0.25Mo (0.38 0.43c). (SAE standard)
Technical Report
·
Sat Jun 01 00:00:00 EDT 1996
·
OSTI ID:591033
Steel bars, forgings and rings, 0.95Cr 0.20Mo (0.38-0.43C), annealed. (SAE standard)
Technical Report
·
Mon May 01 00:00:00 EDT 1995
·
OSTI ID:591033