Coarsening of the Sn-Pb Solder Microstructure in Constitutive Model-Based Predictions of Solder Joint Thermal Mechanical Fatigue
Thermal mechanical fatigue (TMF) is an important damage mechanism for solder joints exposed to cyclic temperature environments. Predicting the service reliability of solder joints exposed to such conditions requires two knowledge bases: first, the extent of fatigue damage incurred by the solder microstructure leading up to fatigue crack initiation, must be quantified in both time and space domains. Secondly, fatigue crack initiation and growth must be predicted since this metric determines, explicitly, the loss of solder joint functionality as it pertains to its mechanical fastening as well as electrical continuity roles. This paper will describe recent progress in a research effort to establish a microstructurally-based, constitutive model that predicts TMF deformation to 63Sn-37Pb solder in electronic solder joints up to the crack initiation step. The model is implemented using a finite element setting; therefore, the effects of both global and local thermal expansion mismatch conditions in the joint that would arise from temperature cycling.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sandia National Lab. (SNL-CA), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 5803
- Report Number(s):
- SAND99-0932J; TRN: AH200115%%115
- Journal Information:
- Journal of Electronic Materials, Other Information: Submitted to Journal of Electronic Materials; PBD: 12 Apr 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Isothermal fatigue behavior of Sn--Pb solder joints
Coarsening of the Sn-Pb solder microstructure in constitutive model-based predictions of solder joint thermal mechanical fatigue