Oxidation and salt corrosion of an Si{sub 2}N{sub 2}O-ZrO{sub 2} composite material
- Univ. of Technology, Goeteborg (Sweden)
- Swedish Ceramic Institute, Goeteborg (Sweden)
The oxidation/corrosion resistance in dry and humid environments of a low-cost, porous Si{sub 2}N{sub 2}O-ZrO{sub 2} composite material has been investigated. The oxidation experiments were carried out in a tube furnace in dry and humid oxygen (10% H{sub 2}O). For the corrosion experiments an aerosol generator was used capable of controlling the salt concentration (NaCl) during the corrosion experiments. The extent of internal oxidation has been found to be dependent on the oxidation temperature. Very good oxidation resistance has been observed at temperatures >1300{degrees}C. It was confirmed that at 1000{degrees}C oxidation occurs homogeneously throughout the specimen while at higher temperatures pore sealing occurs after the initial oxidation.
- OSTI ID:
- 567567
- Report Number(s):
- CONF-960106-; TRN: 98:000275-0034
- Resource Relation:
- Conference: 20. annual conference on composites, advanced ceramics, materials and structures-B, Cocoa Beach, FL (United States), 7-11 Jan 1996; Other Information: PBD: 1996; Related Information: Is Part Of Proceedings of the 20th annual conference on composites, advanced ceramics, materials, and structures - A; Greenhut, V.; PB: 498 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Different Zirconium Contents on the Corrosion Resistance of ZrO{sub 2}-TiO{sub 2} Film-Coated Stainless Steel
Microstructure and short-term oxidation of hot-pressed Si sub 3 N sub 4 /ZrO sub 2 (Y sub 2 O sub 3 ) ceramics