Diamond nucleation under bias conditions
- Institut fuer Technische Physik, Universitaet Erlangen-Nuernberg, Erwin-Rommel-Strasse 1, 91058 Erlangen (Germany)
- Institut fuer Werkstoffwissenschaften, Universitaet Erlangen-Nuernberg, Cauerstr.6, 91058 Erlangen (Germany)
The so-called bias pretreatment allows the growth of heteroepitaxial diamond films by plasma chemical vapor deposition on silicon (100) surfaces. We present plan-view and cross-sectional transmission electron micrographs of the substrate surface at different phases of the bias pretreatment. These observations are augmented by measurements of the etch rates of Si, SiC, and different carbon modifications under plasma conditions and the size distribution of oriented diamond crystals grown after bias pretreatment. Based on these results a new model for diamond nucleation under bias conditions is proposed. First, a closed layer of nearly epitaxially oriented cubic SiC with a thickness of about 10 nm is formed. Subplantation of carbon into this SiC layer causes a supersaturation with carbon and results in the subcutaneous formation of epitaxially oriented nucleation centers in the SiC layer. Etching of the SiC during the bias pretreatment as well as during diamond growth brings these nucleation centers to the sample surface and causes the growth of diamonds epitaxially oriented on the Si/SiC substrate. {copyright} {ital 1998 American Institute of Physics.}
- OSTI ID:
- 565631
- Journal Information:
- Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 1 Vol. 83; ISSN JAPIAU; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of pretreatment bias on the nucleation and growth mechanisms of ultrananocrystalline diamond films via bias-enhanced nucleation and growth: An approach to interfacial chemistry analysis via chemical bonding mapping
Characterization of diamond nucleation enhancing layer formed during bias treatment on silicon
Microstructual study of the alternating current bias-enhanced nucleation and growth of diamond on (001) silicon wafers
Journal Article
·
Sat Jan 31 23:00:00 EST 2009
· Journal of Applied Physics
·
OSTI ID:21186018
Characterization of diamond nucleation enhancing layer formed during bias treatment on silicon
Conference
·
Sat Dec 30 23:00:00 EST 1995
·
OSTI ID:230067
Microstructual study of the alternating current bias-enhanced nucleation and growth of diamond on (001) silicon wafers
Journal Article
·
Sun Jun 01 00:00:00 EDT 1997
· Applied Physics Letters
·
OSTI ID:529995