Effect of resin toughness on the delamination fracture behavior of graphite/epoxy composites
The objective of this dissertation research was to develop improved understanding of the deformation and fracture physics of delamination in resin toughened graphite/epoxy composites. Experiments were conducted in pure mode I, mixed mode I/mode II and pure mode II conditions. A damage dependent J-integral analysis developed by Schapery was shown to have merit in analyzing results from of-axis laminates. Using this analysis, there appears to be an intrinsic delamination fracture toughness for mode I, independent of the fiber orientation or macroscopic modulus of the material. Rubber particle additions to the resin increase the mode I delamination fracture toughness more than they do the mode II delamination toughness. There appears to be a direct correlation between the size of the microcracked crack tip damage zone and the mode I delimination fracture toughness. Analysis of the fractured surface in an SEM can be used to indicate the state of stress but not the crack growth direction.
- Research Organization:
- Texas A and M Univ., College Station (USA)
- OSTI ID:
- 5284272
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microscopic delamination processes and the resulting crack tip strain fields of graphite/epoxy composites
Enhanced mode-II fracture toughness of an epoxy resin due to shear banding
Related Subjects
360303* -- Composite Materials-- Mechanical Properties-- (-1987)
CARBON
COMPOSITE MATERIALS
CRACKS
ELASTOMERS
ELEMENTAL MINERALS
ELEMENTS
EPOXIDES
FRACTURE MECHANICS
GRAPHITE
MATERIALS
MECHANICS
MINERALS
NONMETALS
ORGANIC COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
ORGANIC POLYMERS
PETROCHEMICALS
PETROLEUM PRODUCTS
POLYMERS
RESINS
RUBBERS