Creep and low-cycle fatigue behavior of ferritic Fe-24Cr-4Al alloy in the dynamic strain aging regime: Effect of aluminum addition

Journal Article · Sun Jun 01 04:00:00 EDT 1997 · Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science

DOI:https://doi.org/10.1007/s11661-997-0271-7· OSTI ID:514761

Tjong, S C; Zhu, S M ^[1]

---

1. City Univ. of Hong Kong, Kowloon (Hong Kong). Dept. of Physics and Materials Science

Creep and low-cycle fatigue behavior of ferritic Fe-24Cr-04Al alloy was studied in the temperature range of 673 to 873 K, where dynamic strain aging (DSA) occurrence was found. The DSA of the alloy manifested in the form of serrated flow, negative strain rate sensitivity, and the peak or plateau in the variations of yield strength (YS) and ultimate tensile strength (UTS) with temperature. The characteristic creep behavior of the alloy was experimentally verified as that for a class I solid solution. However, this ferritic alloy showed an anomalous high stress exponent (n = 5.7) and high activation energy (Q{sub c} = 285 kJ/mol) of the secondary creep, which were commonly exhibited by class II solid solutions. During cyclic deformation, the alloy displayed serration in the stress-strain hysteresis loops, increased cyclic hardening, and enhanced planarity of dislocations. On the basis of the observed experimental results and proper analysis, it was proposed that there was strong elastic interaction between solute aluminum atoms and dislocations in the DSA temperature domain. The anomalous creep and fatigue features were interpreted in terms of the interaction of aluminum with the dislocations.

• Sponsoring Organization: USDOE
• OSTI ID: 514761
• Journal Information: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, Journal Name: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science Journal Issue: 6 Vol. 28; ISSN MMTAEB; ISSN 1073-5623
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALUMINIUM ALLOYS
CHROMIUM ALLOYS
CREEP
DISLOCATIONS
FATIGUE
IRON BASE ALLOYS
STRAIN AGING
ULTIMATE STRENGTH
YIELD STRENGTH