Interfacial segregation in oxide scales on NiCrAl-based alloys
- Oak Ridge National Lab., TN (United States). Metals and Ceramics Div.
Previous studies addressing the segregation of reactive elements in protective oxide scales and their beneficial effect on scale adhesion have primarily concentrated on primary alumina-formers. In this study the isothermal oxidation behavior of three NiCrAl alloys, which form complex oxide scales was studied in air at 1,473 K for 100 hrs. The resulting oxide scales were characterized by scanning electron microscopy (SEM) and cross=sectional transmission electron microscopy (TEM) techniques. Segregation at internal interfaces was analyzed in the STEM mode on a Philips CM200 FEG-TEM, operated at 200 kV and equipped with a Link ultrathin-window EDS detector. The probe size of the electron beam was about 1.5 nm. Spectra were recorded with grain boundaries oriented parallel to the electron beam. The oxide scale on Rene N5 ({approximately}5 {micro}m) consists of columnar {alpha}-Al{sub 2}O{sub 3} at the bottom ({approximately}4 {micro}m) and a mixed layer of spinel (Ni, Co, Ta) (Al,Cr){sub 2}O{sub 4} and {alpha}-Al{sub 2}O{sub 3} ({approximately}1 {micro}m) at the top. On Ni-7Cr-6.5Al+Y, the scale ({approximately}9 {micro}m) consists mainly of columnar Cr-doped {alpha}-Al{sub 2}O{sub 3}. Ni-10Cr-10Al+Y forms an oxide scale ({approximately}8 {micro}m) that consists mainly of columnar Cr-doped {alpha}-Al{sub 2}O{sub 3}. The results are consistent with previous results on primary alumina-formers.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Research, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 505349
- Report Number(s):
- CONF-970834--12; ON: DE97005155
- Country of Publication:
- United States
- Language:
- English
Similar Records
The microstructure and mechanical reliability of alumina scales and coatings
Grain boundary segregation of cation dopants in {alpha}-Al{sub 2}O{sub 3} scales
STEM and APT characterization of scale formation on a La,Hf,Ti-doped NiCrAl model alloy
Conference
·
Mon Sep 01 00:00:00 EDT 1997
·
OSTI ID:520703
Grain boundary segregation of cation dopants in {alpha}-Al{sub 2}O{sub 3} scales
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:459331
STEM and APT characterization of scale formation on a La,Hf,Ti-doped NiCrAl model alloy
Journal Article
·
Fri Apr 06 20:00:00 EDT 2018
· Micron
·
OSTI ID:1814407